Simulacijska analiza na makrostrukturi okruglog trupca od posebnog vertikalno ljevanog čelika

Lian-wang Zhang ; School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, P. R. China
Jing Li ; School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, P. R. China
Zhi-lin Wang ; Zhongyuan Special Steel CO. Ltd, Jiyuan, Henan 454650, P. R. China
Yi-qun Wang ; Zhongyuan Special Steel CO. Ltd, Jiyuan, Henan 454650, P. R. China
Chang-jun Xu ; School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, P. R. China
Sheng-li Li ; School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051, P. R. China


Puni tekst: engleski pdf 2.754 Kb

str. 1821-1824

preuzimanja: 447

citiraj

Puni tekst: hrvatski pdf 2.754 Kb

str. 1821-1824

preuzimanja: 397

citiraj


Sažetak

Ovaj rad daje analizu okruglog trupca 42CrMo vertikalno ljevanog. Temelji se na parametrima procesa kontinuiranog lijevanja ZhongYuan specijalnog čelika i parametrima CAFE nukleacije, usvojenom metodom "ProCAST chip-moving boundary" za provođenje numeričke simulacije okruglog trupca. Simulacijski i praktični slučajevi imaju istu makrostrukturnu morfologiju, okrugla kladica ima središnji istoosni kristal od 41,2 %. Kako je smanjeno pregrijavanje tekućeg čelika i intenziteta hlađenja, prosječni radijus kristala se smanjio, broj kristala se povećao, a makrostruktura je pokazala trend progresivnog razrađivanja.

Ključne riječi

42CrMo; makrosturktura; veliki okrugli trupac; vertikalno ljevanje