Zamorna svojstva zavarenih spojeva tankog lima od ugljičnog čelika obrađenog nitrooksidacijom

Ivan Michalec ; Slovak University of Technology in Bratislava, Faculty of Materials Science and Technology in Trnava, Institute of Production Technologies, Paulínska 16, 91701 Trnava, Slovakia
Milan Marônek orcid.org/0000-0002-4716-8092 ; Slovak University of Technology in Bratislava, Faculty of Materials Science and Technology in Trnava, Institute of Production Technologies, Paulínska 16, 91701 Trnava, Slovakia
Jozef Bárta orcid.org/0000-0003-0607-4433 ; Slovak University of Technology in Bratislava, Faculty of Materials Science and Technology in Trnava, Institute of Production Technologies, Paulínska 16, 91701 Trnava, Slovakia
František Nový ; University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering, Univerzitná 1, 010 26 Žilina, Slovakia

Sažetak

Nisko ugljični čelik DC 01 (EN 10130-91) obrađen postupkom nitrooksidacije značajno je povećao mehanička svojstva kao i otpornost na atmosfersku koroziju. To je povećanje nastalo zbog postojanja površinskih nitridnih i oksidnih slojeva. Do sada su predlagani odgovarajući postupci zavarivanja za tako obrađivane čelične limove, od kojih se zavarivanje čvrstog tijela laserskim snopom (solid-state laser beam welding) smatralo najpogodnijim. Cilj je ovoga rada bio odrediti zamorna svojstva laserom zavarenih spojeva materijala obrađenog nitrooksidacijom. Provedena je i fraktografska analiza. Ispitivanja na zamor su se provodila kod opterećenja pri savijanju s frekvencijom od 20 kHz i sinusoidalnim simetričnim ciklusom. Rezultati su dokazali da se postupkom nitrooksidacije značajno poboljšavaju zamorna svojstva zavarenih spojeva.

Ključne riječi

nitrooksidacija; zamor; S-N dijagram