Possible Improvements of Clinical Properties of Dental Composite Materials with Pulsed Blue Laser Curing

Zrinka Tarle ; School of Dental Medicine, University of Zagreb, Gundulićeva 5, HR-10000 Zagreb, Croatia
Andrej Meniga ; School of Dental Medicine, University of Zagreb, Gundulićeva 5, HR-10000 Zagreb, Croatia
Mira Ristić ; Rugjer Bo{kovi} Institute, Bijenička 54, HR-10000 Zagreb, Croatia
Jozo Šutalo ; School of Dental Medicine, University of Zagreb, Gundulićeva 5, HR-10000 Zagreb, Croatia
Goran Pichler ; Institute of Physics, Bijenička 46, HR-10000 Zagreb, Croatia

Sažetak

Despite considerable improvements of dental composite materials, the present-day composite resins still suffer from two major shortcomings that limit their use: inadequate degree of conversion and polymerization shrinkage. The objective of this study was to evaluate the degree of conversion and polymerization shrinkage of two hybrid and two microfilled composite materials cured by pulsed blue dye laser pumped XeCl excimer laser at 308 nm and the standard curing unit. The degree of conversion was measured by a Perkin Elmer FTIR spectrometer at the surface of the material and at a 3.0 mm depth. Statistical analysis (ANOVA p < 0.05) showed a significantly higher degree of conversion values in the case of pulsed laser. Polymerization shrinkage measured by a pycnometer showed significantly lower values in the case of pulsed laser curing for six out of eight materials observed. The saturation effect in the material illuminated by monochromatic blue pulsed laser light (468 nm) may be responsible for the higher degree of conversion, while the relaxation of the molecules between nanopulses may lead to a reduced polymerization shrinkage.