Examining properties of arc sprayed nanostructured coatings

A. Czupryński ; Silesian University of Technology, Gliwice, Poland
J. Gorka ; Silesian University of Technology, Gliwice, Poland
M. Adamiak ; Silesian University of Technology, Gliwice, Poland

Sažetak

The article presents the results of examining properties of arc sprayed coating obtained with nano-alloy on the iron matrix with a high amount of fine carbide precipitates sprayed on non-alloyed steel plates intended for high temperature operation. Powder metal cored wire EnDOtec DO*390N 1,6 mm diameter, was used to produce, dense, very high abrasion and erosion resistant coatings approx. 1,0 mm thick. Nano-material coatings characterization was done to determine abrasion resistance, erosion resistance, adhesion strength, hardness as well as metallographic examinations. Results have proved high properties of arc sprayed nano-material coatings and have shown promising industrial applications.

Ključne riječi

coating; wire arc spraying; nano-alloys; abrasive and erosion wear; adhesion strength

Hrčak ID:

146489

URI

https://hrcak.srce.hr/146489

Datum izdavanja:

1.4.2016.

Posjeta: 1.391 *