HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method

Jerzy Jozwik ; Mechanical Engineering Faculty, Lublin University of Technology, Nadbystrzycka Street, 36, 20-618 Lublin, Poland
Krzysztof Dziedzic ; Mechanical Engineering Faculty, Lublin University of Technology, Nadbystrzycka Street, 36, 20-618 Lublin, Poland
Ireneusz Usydus ; The Institute of Technical Sciences and Aviation, The State School of Higher Education, Pocztowa Street, 54, 22-100 Chelm, Poland
Pero Raos orcid id orcid.org/0000-0001-9263-1325 ; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić-Mažuranić 2, 35000 Slavonski Brod, Croatia
Grzegorz M. Krolczyk ; Opole University of Technology, 76 Prószkowska Street, 45-758 Opole, Poland


Puni tekst: hrvatski pdf 1.944 Kb

str. 1405-1409

preuzimanja: 373

citiraj

Puni tekst: engleski pdf 1.944 Kb

str. 1405-1409

preuzimanja: 315

citiraj


Sažetak

The paper reviews the process of surface layer development with the use of carbonitriding and carbonitriding with oxidation. Employed for that purpose was a modern and ecological method called ZeroFlow. Research was carried out using HS 6-5-2 steel. Single-component nitrifying atmosphere of ammonia NH3 was applied. The temperature of the processes was 570 °C. Diffusion layers were obtained on the steel. The thickness of the layers achieved during the microstructural research equalled from about 125 μm after carbonitriding with oxidation to about 187 μm after carbonitriding. Surface hardness HV1 was the highest for the carbonitrided layer - 1027 HV1, whereas in the case of carbonitriding with oxidation it amounted to 1018 HV1. As far as surface hardness HV30 is concerned, it was at the level of 813 HV30 for the carbonitrided layer and 795 HV30 for carbonitriding with oxidation. Surface hardness test results indicate surface layer hardening.

Ključne riječi

carbonitriding; microhardness; nitriding; oxidation; surface layer