Termofizikalna i strukturalna studija IN 792-5A niklove superlegure

S. Zlá ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic
J. Dobrovská ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic
B. Smetana ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic
M. Žaludová ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic
V. Vodárek ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic
K. Konečná ; VŠB-TU Ostrava, FMME, Ostrava, Czech Republic

Puni tekst: engleski, pdf (273 KB) str. 83-86 preuzimanja: 634* citiraj
APA 6th Edition
Zlá, S., Dobrovská, J., Smetana, B., Žaludová, M., Vodárek, V. i Konečná, K. (2012). Thermophysical and structural study of IN 792-5A nickel based superalloy. Metalurgija, 51 (1), 83-86. Preuzeto s https://hrcak.srce.hr/71180
MLA 8th Edition
Zlá, S., et al. "Thermophysical and structural study of IN 792-5A nickel based superalloy." Metalurgija, vol. 51, br. 1, 2012, str. 83-86. https://hrcak.srce.hr/71180. Citirano 06.08.2021.
Chicago 17th Edition
Zlá, S., J. Dobrovská, B. Smetana, M. Žaludová, V. Vodárek i K. Konečná. "Thermophysical and structural study of IN 792-5A nickel based superalloy." Metalurgija 51, br. 1 (2012): 83-86. https://hrcak.srce.hr/71180
Harvard
Zlá, S., et al. (2012). 'Thermophysical and structural study of IN 792-5A nickel based superalloy', Metalurgija, 51(1), str. 83-86. Preuzeto s: https://hrcak.srce.hr/71180 (Datum pristupa: 06.08.2021.)
Vancouver
Zlá S, Dobrovská J, Smetana B, Žaludová M, Vodárek V, Konečná K. Thermophysical and structural study of IN 792-5A nickel based superalloy. Metalurgija [Internet]. 2012 [pristupljeno 06.08.2021.];51(1):83-86. Dostupno na: https://hrcak.srce.hr/71180
IEEE
S. Zlá, J. Dobrovská, B. Smetana, M. Žaludová, V. Vodárek i K. Konečná, "Thermophysical and structural study of IN 792-5A nickel based superalloy", Metalurgija, vol.51, br. 1, str. 83-86, 2012. [Online]. Dostupno na: https://hrcak.srce.hr/71180. [Citirano: 06.08.2021.]

Sažetak
Rad daje studiju temperature faznih transformacija niklove superslitine IN792-5A primjenom DTA metode te eksperimentalnog laboratorijskog sustava za simulaciju termalne analize SETARAM Setsys 18TM. Uzorci su uzeti iz početnog stanja legure i održavani definiranim brzinama (1, 5, 10 i 20 °C•min-1) i poslije ohlađeni kontroliranim brzinama. Uzorci su prije i poslije DTA analiza bili predmet fazne analize s primjenom skeninga elektronske mikroskopije (JCXA 733) dopunjeno s energi disperznom analizom EDAX (EDAM 3).

Ključne riječi
DTA-metoda; IN792-5A; temperature fazne transformacije; skening elektronske mikroskopije