Wear and corrosion performances of new friction materials for automotive industry

R. Samur ; Department of Metallurgy, Faculty of Technical Education, Marmara University, 34722, Goztepe, Istanbul, Turkey
A. Demir ; Alemdag Cad. Turk Telekom Fabrika Yani Haldun ALAGAS Spor Kompleksi Umraniye, Istanbul, Turkey

Puni tekst: engleski, pdf (195 KB) str. 94-96 preuzimanja: 698* citiraj
APA 6th Edition
Samur, R. i Demir, A. (2012). Wear and corrosion performances of new friction materials for automotive industry. Metalurgija, 51 (1), 94-96. Preuzeto s https://hrcak.srce.hr/71183
MLA 8th Edition
Samur, R. i A. Demir. "Wear and corrosion performances of new friction materials for automotive industry." Metalurgija, vol. 51, br. 1, 2012, str. 94-96. https://hrcak.srce.hr/71183. Citirano 28.09.2021.
Chicago 17th Edition
Samur, R. i A. Demir. "Wear and corrosion performances of new friction materials for automotive industry." Metalurgija 51, br. 1 (2012): 94-96. https://hrcak.srce.hr/71183
Harvard
Samur, R., i Demir, A. (2012). 'Wear and corrosion performances of new friction materials for automotive industry', Metalurgija, 51(1), str. 94-96. Preuzeto s: https://hrcak.srce.hr/71183 (Datum pristupa: 28.09.2021.)
Vancouver
Samur R, Demir A. Wear and corrosion performances of new friction materials for automotive industry. Metalurgija [Internet]. 2012 [pristupljeno 28.09.2021.];51(1):94-96. Dostupno na: https://hrcak.srce.hr/71183
IEEE
R. Samur i A. Demir, "Wear and corrosion performances of new friction materials for automotive industry", Metalurgija, vol.51, br. 1, str. 94-96, 2012. [Online]. Dostupno na: https://hrcak.srce.hr/71183. [Citirano: 28.09.2021.]

Sažetak
In this study, after a NiCr bond layer was deposited on a pearlitic, grey cast iron rotor disc of the kind used in a production passenger car (Toyota Corolla 1600 cc), Cr3C2-NiCr and Al2O3-TiO2powders were sprayed using High Velocity Oxygen Fuel(HVOF) and plasma spray processes, respectively. The discs were subjected to cosmetic corrosion test according to SAE J2334 test standard. Additionally, wear tests were carried out using a reciprocating wear tester by rubbing a 10 mm diameter Al2O3 ball on the specimens machined from rotor discs in salt solution. It was found that the Cr3C2-NiCr coating (HSCN) sprayed using HVOF method exhibited highest hardness and highest corrosion and wear resistances.

Ključne riječi
wear; friction; corrosion; friction material; coating; automotive industry