Increasing of hot workability of 1.3302HIGH speed steel

D. Bombač ; Department of Materials and Metallurgy, Universityof Ljubljana, Ljubljana, Slovenia
M. Terčelj ; Department of Materials and Metallurgy, Universityof Ljubljana, Ljubljana, Slovenia
M. Fazarinc ; Department of Materials and Metallurgy, Universityof Ljubljana, Ljubljana, Slovenia
P. Fajfar ; Department of Materials and Metallurgy, Universityof Ljubljana, Ljubljana, Slovenia

Sažetak

Laboratory investigation of hot workability of 1.3302 high speed steel was carried out and its improving was achieved. Hot compression tests for the determination of optimal soaking temperature as well as for the study of hot workability in temperature range 1150-850 ºC, strain rates range 0,001-6 s–1 and applied strain up to 0,9 were performed. Microstructure of deformed specimen was analyzed. Apparent activation energies for hot working for upper and for lower temperature range were calculated. Onsets of dynamical recrystallization for applied deformation conditions on the basis of calculated strain hardening ratewere determined. Extending of hot working temperature range at its lower limit, i.e. down to 850 ºC, by applying optimal soaking temperature was obtained.

Ključne riječi

1.3302 HSS; hot compression; dynamic recrystallization; strain hardening rate