Influence of Portland Cement Class on the Corrosion Rate of Steel Reinforcement in Cement Mortar Caused by Penetrating Chloride and Sulfate from the Environment
F. Bikić
; Fakultet za metalurgiju i materijale, Univerzitet u Zenici, Bosna i Hercegovina
M. Rizvanović
; Fakultet za metalurgiju i materijale, Univerzitet u Zenici, Bosna i Hercegovina
M. Cacan
; Prirodno-matematički fakultet, Univerzitet u Sarajevu, Bosna i Hercegovina
Sažetak
The influence of portland cement class on the corrosion rate of steel reinforcement in cement mortar caused by penetrating chloride or sulfate from the environment in already hardened cement mortar is investigated in this paper. Three classes of portland cement have been used for the tests, PC 35, PC 45 and PC 55. Cylindrical samples of cement mortar with steel reinfor- cement in the middle were treated 6 months at room temperature in the following solutions: w(SO42-) = 2.1 % and w(Cl-) = 5 %. Two techniques have been used for testing corrosion rate of steel reinforcement in cement mortar: Tafel extrapolation technique and potentiodynamic polarization technique. Investigations were conducted by potentiostat/galvanostat Princeton Applied Research 263A-2 with the software PowerCORR®. The results of both techniques indi-cate the most active corrosion of steel reinforcement in the samples prepared from cement PC 35 in both treated solutions, while the lowest corrosion of the steel reinforcement was observed in cement samples prepared from cement PC 55. This conclusion was drawn by analyzing the results shown in Figs. 1–4. Comparing corrosion current density of samples, working electrodes, Figs. 1 and 2, Table 2, the results show the most stable corrosion of steel reinforcement in samples prepared from cement PC 55, and the most active corrosion in samples prepared from ce- ment PC 35. The most active corrosion in samples prepared from cement PC 35 is evident from the positions of the open circuit potentials whose values are less for samples prepared from cement PC 35 in both the treated solution, Figs. 1 and 2, Table 2. Comparison of the anodic polarization curves of the working electrodes in both the treated solutions, Figs. 3 and 4, also shows that the intensity of corrosion is the largest for the working electrodes prepared from cement PC 35 and the smallest for the working electrodes prepared from cement PC 55. Investigation results should be considered as preliminary. To make the recommendations for the construction of reinforced concrete structures in the maritime environment the impact of sulphates on concrete and steel bars should be investigated.
Ključne riječi
Cement class; Cement mortar; Corrosion rate of steel reinforcement; chloride; sulfate