Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement

Sanja Štefančić ; Dental Polyclinic Zagreb, Zagreb, Croatia
Lidija Ćurković ; Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Zagreb, Croatia
Gorana Baršić ; Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Zagreb, Croatia
Marijana Majić-Renjo ; Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Zagreb, Croatia
Ketij Mehulić ; School of Dental Medicine, University of Zagreb, Zagreb, Croatia

Puni tekst: engleski, pdf (448 KB) str. 163-168 preuzimanja: 355* citiraj
APA 6th Edition
Štefančić, S., Ćurković, L., Baršić, G., Majić-Renjo, M. i Mehulić, K. (2013). Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement. Acta stomatologica Croatica, 47 (2), 163-168. https://doi.org/10.15644/asc47/2/8
MLA 8th Edition
Štefančić, Sanja, et al. "Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement." Acta stomatologica Croatica, vol. 47, br. 2, 2013, str. 163-168. https://doi.org/10.15644/asc47/2/8. Citirano 15.07.2020.
Chicago 17th Edition
Štefančić, Sanja, Lidija Ćurković, Gorana Baršić, Marijana Majić-Renjo i Ketij Mehulić. "Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement." Acta stomatologica Croatica 47, br. 2 (2013): 163-168. https://doi.org/10.15644/asc47/2/8
Harvard
Štefančić, S., et al. (2013). 'Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement', Acta stomatologica Croatica, 47(2), str. 163-168. https://doi.org/10.15644/asc47/2/8
Vancouver
Štefančić S, Ćurković L, Baršić G, Majić-Renjo M, Mehulić K. Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement. Acta stomatologica Croatica [Internet]. 2013 [pristupljeno 15.07.2020.];47(2):163-168. https://doi.org/10.15644/asc47/2/8
IEEE
S. Štefančić, L. Ćurković, G. Baršić, M. Majić-Renjo i K. Mehulić, "Investigation of Glazed Y-TZP Dental Ceramics Corrosion by Surface Roughness Measurement", Acta stomatologica Croatica, vol.47, br. 2, str. 163-168, 2013. [Online]. https://doi.org/10.15644/asc47/2/8
Puni tekst: hrvatski, pdf (448 KB) str. 163-168 preuzimanja: 188* citiraj
APA 6th Edition
Štefančić, S., Ćurković, L., Baršić, G., Majić-Renjo, M. i Mehulić, K. (2013). Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju. Acta stomatologica Croatica, 47 (2), 163-168. https://doi.org/10.15644/asc47/2/8
MLA 8th Edition
Štefančić, Sanja, et al. "Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju." Acta stomatologica Croatica, vol. 47, br. 2, 2013, str. 163-168. https://doi.org/10.15644/asc47/2/8. Citirano 15.07.2020.
Chicago 17th Edition
Štefančić, Sanja, Lidija Ćurković, Gorana Baršić, Marijana Majić-Renjo i Ketij Mehulić. "Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju." Acta stomatologica Croatica 47, br. 2 (2013): 163-168. https://doi.org/10.15644/asc47/2/8
Harvard
Štefančić, S., et al. (2013). 'Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju', Acta stomatologica Croatica, 47(2), str. 163-168. https://doi.org/10.15644/asc47/2/8
Vancouver
Štefančić S, Ćurković L, Baršić G, Majić-Renjo M, Mehulić K. Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju. Acta stomatologica Croatica [Internet]. 2013 [pristupljeno 15.07.2020.];47(2):163-168. https://doi.org/10.15644/asc47/2/8
IEEE
S. Štefančić, L. Ćurković, G. Baršić, M. Majić-Renjo i K. Mehulić, "Ispitivanje hrapavosti površine glazirane Y-TZP zubne keramike nakon izlaganja korozivnom mediju", Acta stomatologica Croatica, vol.47, br. 2, str. 163-168, 2013. [Online]. https://doi.org/10.15644/asc47/2/8

Sažetak
Introduction: Among dental applications, the zirconia based ceramics are widespread because of their general properties. The changes in superficial surface roughness correspond to the structural changes in the material caused by the influence of corrosion. The aim of this study was to determine chemical stability of glazed Y-TZP using surface roughness measurements. Materials and methods: Five samples of Y-TZP material BruxZir (Glidewell Laboratories © 2012.) with the addition of pigment A3 were sintered, polished and glazed to imitate the finishing process in producing monolithic crowns. After determining the mass of the sample, each sample was immersed in 10 ml of 4 wt. % CH3COOH aqueous solution. The roughness was measured five times before and after immersion. Results: All measured roughness parameters have significantly increased, showing higher penetration depth in all surface areas after immersion in 4 wt. % CH3COOH aqueous solution compared to the initial values. Weight loss of investigated dental ceramics samples was 2.45 mg/cm2 ± 0.026. Conclusion: Highly acidic conditions augment surface roughness of Y-TZP glazed dental ceramics.