XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja

Krzysztof Rokosz ; Division of Surface Electrochemistry and Technology, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Tadeusz Hryniewicz ; Division of Surface Electrochemistry and Technology, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Ryszard Rokicki ; ELECTROBRIGHT, 142 W. Main St., Macungie, PA 18062, USA

Puni tekst: hrvatski, pdf (1 MB) str. 799-805 preuzimanja: 612* citiraj
APA 6th Edition
Rokosz, K., Hryniewicz, T. i Rokicki, R. (2014). XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja. Tehnički vjesnik, 21 (4), 799-805. Preuzeto s https://hrcak.srce.hr/126075
MLA 8th Edition
Rokosz, Krzysztof, et al. "XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja." Tehnički vjesnik, vol. 21, br. 4, 2014, str. 799-805. https://hrcak.srce.hr/126075. Citirano 01.03.2021.
Chicago 17th Edition
Rokosz, Krzysztof, Tadeusz Hryniewicz i Ryszard Rokicki. "XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja." Tehnički vjesnik 21, br. 4 (2014): 799-805. https://hrcak.srce.hr/126075
Harvard
Rokosz, K., Hryniewicz, T., i Rokicki, R. (2014). 'XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja', Tehnički vjesnik, 21(4), str. 799-805. Preuzeto s: https://hrcak.srce.hr/126075 (Datum pristupa: 01.03.2021.)
Vancouver
Rokosz K, Hryniewicz T, Rokicki R. XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja. Tehnički vjesnik [Internet]. 2014 [pristupljeno 01.03.2021.];21(4):799-805. Dostupno na: https://hrcak.srce.hr/126075
IEEE
K. Rokosz, T. Hryniewicz i R. Rokicki, "XPS mjerenja cijevi od biomaterijala AISI 316LVM SS nakon magnetoelektropoliranja", Tehnički vjesnik, vol.21, br. 4, str. 799-805, 2014. [Online]. Dostupno na: https://hrcak.srce.hr/126075. [Citirano: 01.03.2021.]
Puni tekst: engleski, pdf (1 MB) str. 799-805 preuzimanja: 249* citiraj
APA 6th Edition
Rokosz, K., Hryniewicz, T. i Rokicki, R. (2014). XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing. Tehnički vjesnik, 21 (4), 799-805. Preuzeto s https://hrcak.srce.hr/126075
MLA 8th Edition
Rokosz, Krzysztof, et al. "XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing." Tehnički vjesnik, vol. 21, br. 4, 2014, str. 799-805. https://hrcak.srce.hr/126075. Citirano 01.03.2021.
Chicago 17th Edition
Rokosz, Krzysztof, Tadeusz Hryniewicz i Ryszard Rokicki. "XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing." Tehnički vjesnik 21, br. 4 (2014): 799-805. https://hrcak.srce.hr/126075
Harvard
Rokosz, K., Hryniewicz, T., i Rokicki, R. (2014). 'XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing', Tehnički vjesnik, 21(4), str. 799-805. Preuzeto s: https://hrcak.srce.hr/126075 (Datum pristupa: 01.03.2021.)
Vancouver
Rokosz K, Hryniewicz T, Rokicki R. XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing. Tehnički vjesnik [Internet]. 2014 [pristupljeno 01.03.2021.];21(4):799-805. Dostupno na: https://hrcak.srce.hr/126075
IEEE
K. Rokosz, T. Hryniewicz i R. Rokicki, "XPS measurements of AISI 316LVM SS biomaterial tubes after magnetoelectropolishing", Tehnički vjesnik, vol.21, br. 4, str. 799-805, 2014. [Online]. Dostupno na: https://hrcak.srce.hr/126075. [Citirano: 01.03.2021.]

Sažetak
XPS (X-ray Photoelectron Spectroscopy) mjerenja obavljena su na uzorcima cijevi od biomaterijala AISI 316LVM nehrđajućeg čelika koji služi za stentove, nakon uobičajenog elektropoliranja (EP) i magnetoelektropoliranja (MEP). Nakon izvršenih operacija elektropoliranja, uzorci su se, zapakirani u foliji, držali otprilike četiri godine. Rezultati XPS analize pokazuju značajnu razliku u vrijednostima mjerenja i računanja, ovisno o metodi površinske obrade: EP i/ili MEP. Izračunat je sastav površinskog sloja čelika i PREN (ekvivalentni broj otpornosti na točkastu eroziju). Najveći su iznosi tih vrijednosti dobiveni na uzorcima poslije MEP-a kada su i vrijednosti spojeva kroma (Cr 2p) i molibdena (Mo 3d) porasle više od tri puta u odnosu na te vrijednosti nakon postupka EP. Izračunati PRENMEP (Fe, Cr, Mo, Mn, Ni, P, S, O) = 16,37, s PRENMEP (Fe, Cr, Mo, Mn, Ni, P, S) = 36,89, u odnosu na PRENEP (Fe, Cr, Mo, Mn, Ni, P, S, O) = 3,12, s PRENEP (Fe, Cr, Mo, Mn, Ni, P, S) = 8,53. Postignuti rezultati ukazuju na korisno i neobično djelovanje magnetskog polja tijekom MEP-a.

Ključne riječi
cijevi od biomaterijala 316LVM SS; magnetoelektropoliranje MEP; PREN (ekvivalentni broj otpornosti na točkastu eroziju); usporedba XPS rezultata