Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling

H. Dyja
S. Mroz
Z. Stradomski

Puni tekst: engleski, pdf (529 KB) str. 185-191 preuzimanja: 526* citiraj
APA 6th Edition
Dyja, H., Mroz, S. i Stradomski, Z. (2003). Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling. Metalurgija, 42 (3), 185-191. Preuzeto s https://hrcak.srce.hr/128452
MLA 8th Edition
Dyja, H., et al. "Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling." Metalurgija, vol. 42, br. 3, 2003, str. 185-191. https://hrcak.srce.hr/128452. Citirano 20.09.2019.
Chicago 17th Edition
Dyja, H., S. Mroz i Z. Stradomski. "Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling." Metalurgija 42, br. 3 (2003): 185-191. https://hrcak.srce.hr/128452
Harvard
Dyja, H., Mroz, S., i Stradomski, Z. (2003). 'Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling', Metalurgija, 42(3), str. 185-191. Preuzeto s: https://hrcak.srce.hr/128452 (Datum pristupa: 20.09.2019.)
Vancouver
Dyja H, Mroz S, Stradomski Z. Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling. Metalurgija [Internet]. 2003 [pristupljeno 20.09.2019.];42(3):185-191. Dostupno na: https://hrcak.srce.hr/128452
IEEE
H. Dyja, S. Mroz i Z. Stradomski, "Properties of Joint in the Bimetallic Rods Cu-Al and Cu-Steel After Explosive Cladding and the Process of Rolling", Metalurgija, vol.42, br. 3, str. 185-191, 2003. [Online]. Dostupno na: https://hrcak.srce.hr/128452. [Citirano: 20.09.2019.]

Sažetak
In the paper the microhardness, the microstructure and the bond strength of interface of bimetallic joint on the cross sections of the test bar have been investigated. For the experimental analysis, a bimetallic bar was manufactured using an explosive technique method and the process of rolling. For tests, 23 sets of specimens were prepared each consisting of copper tubes (grade M1-E), rolled steel rods (grade St3S), drawn rods (grade 55) and aluminium rods (grade PA6). The copper tubes and the steel and aluminium rods had different diameters, owing to which different distances between the rods and the internal tube walls were obtained. The results of the research show a significant deviation in microhardness distribution in the both layers near the joining border.