Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing

B. Piekarski
M. Garbiak

Puni tekst: engleski, pdf (535 KB) str. 77-82 preuzimanja: 175* citiraj
APA 6th Edition
Piekarski, B. i Garbiak, M. (2002). Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing. Metalurgija, 41 (2), 77-82. Preuzeto s https://hrcak.srce.hr/128590
MLA 8th Edition
Piekarski, B. i M. Garbiak. "Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing." Metalurgija, vol. 41, br. 2, 2002, str. 77-82. https://hrcak.srce.hr/128590. Citirano 23.02.2020.
Chicago 17th Edition
Piekarski, B. i M. Garbiak. "Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing." Metalurgija 41, br. 2 (2002): 77-82. https://hrcak.srce.hr/128590
Harvard
Piekarski, B., i Garbiak, M. (2002). 'Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing', Metalurgija, 41(2), str. 77-82. Preuzeto s: https://hrcak.srce.hr/128590 (Datum pristupa: 23.02.2020.)
Vancouver
Piekarski B, Garbiak M. Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing. Metalurgija [Internet]. 2002 [pristupljeno 23.02.2020.];41(2):77-82. Dostupno na: https://hrcak.srce.hr/128590
IEEE
B. Piekarski i M. Garbiak, "Effect of Nb and Ti on Microstructure and Mechanical Properties of 30% Ni / 18% Cr Cast Steel After Annealing", Metalurgija, vol.41, br. 2, str. 77-82, 2002. [Online]. Dostupno na: https://hrcak.srce.hr/128590. [Citirano: 23.02.2020.]

Sažetak
The study discusses the microstructure and mechanical properties of eight tested 0.3 % C -30 % Ni - 18 % Cr cast steels stabilized with niobium and titanium after annealing in the cycle of 900 °C / 300 h. The niobium content in the cast steels varied from 0.0 to 2.0 % and that of titanium from 0.0 to 1.2 % by weight. Microstructure was examined using both light microscope and a scanning electron microscope with Link IS-IS attachement as well as an X-ray diffractometer. Depending on the chemical composition of cast steel, the following phases were identified: carbides of MC and M23C6 type and a phase rich in silicon, nickel, niobium and / or titanium, which was supposed to be a phase G. Relationships between the microstructure and mechanical properties of cast steel at 20 and 900 °C were examined as well.