Analysis of the effects of electromagnetic stirring on solidification structure of bearing steel

B. Wang ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China; Department of Engineering, University ofLeicester, Leicester, UK
Z. G. Yang ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China; Special Steel Plant, Laiwu Iron & Steel Co. Ltd., Laiwu,China
X. F. Zhang ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China
Y. T. Wang ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China
C. P. Nie ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China
Q. Liu ; StateKey Laboratory of Advanced Metallurgy, University of Science andTechnology Beijing, Beijing, China
H. B. Dong ; Department of Engineering, University ofLeicester, Leicester, UK


Puni tekst: engleski pdf 224 Kb

str. 327-330

preuzimanja: 1.812

citiraj


Sažetak

In the current study, a 260 mm × 300 mm bloom mould was investigated, on which a method combining finite element and finite volume methods was applied to study the impacts of electromagnetic stirring on molten steel flow and heat transfer, and then t he solidification structure of steel was tested. The obtained simulation results pertaining to magnetic fields were consistent with the onsite measured data. For the 260 mm × 300 mm bloom continuous casting of bearing steel, the appropriate value of current intensity of electromagnetic stirring was found to be 300 A.

Ključne riječi

bearing steel; bloom; continuous casting; electromagnetic stirring; solidification structure