The possibility of tribopair lifetime extending by welding of quenched and tempered stainless steel with quenched and tempered carbon steel
V. Marušić
; Josip Juraj Strossmayer Universityof Osijek, Mechanical Engineering Faculty in Slavonski Brod, Croatia
I. Samardžić
; Josip Juraj Strossmayer Universityof Osijek, Mechanical Engineering Faculty in Slavonski Brod, Croatia
I. Budić
; Josip Juraj Strossmayer Universityof Osijek, Mechanical Engineering Faculty in Slavonski Brod, Croatia
L. Marušić
; University of Applied Sciences in Slavonski Brod, Croatia
Sažetak
In the conditions of tribocorrosion wear, extending of parts lifetime could be achieved by using stainless steel,which is hardened to sufficiently high hardness. In the tribosystem bolt/ bushing shell/link plate of the bucket elevator transporter conveyor machine, the previously quenched and tempered martensitic stainless steel for bolts is hardened at ≈47 HRC and welded with the quenched and tempered high yield carbon steel for bolts. Additional material, based on Cr-Ni-Mo (18/8/6) is used. The microstructure and hardness of welded samples are tested. On the tensile tester, resistance of the welded joint is tested with a simulated experiment. Dimensional control of worn tribosystem elements was performed after six months of service.
Ključne riječi
welded joint; martensitic stainless steel; tribopair; carbon steel; life time