Heat treatment influence on clad dissimilar joints weakness
Branko Mateša
; Mechanical Engineering Faculty in Slavonski Brod, J. J. Strossmayer University of Osijek, Trg Ivane Brlić Mažuranić 2, 35 000 Slavonski Brod, Croatia
Ivan Samardžić
; Mechanical Engineering Faculty in Slavonski Brod, J. J. Strossmayer University of Osijek, Trg Ivane Brlić Mažuranić 2, 35 000 Slavonski Brod, Croatia
Marko Dunđer
; Faculty of Philosophy, University of Rijeka, Department of Polytechnic, Omladinska 14, 51 000 Rijeka, Croatia
APA 6th Edition Mateša, B., Samardžić, I. i Dunđer, M. (2014). Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja. Tehnički vjesnik, 21 (5), 1035-1040. Preuzeto s https://hrcak.srce.hr/129050
MLA 8th Edition Mateša, Branko, et al. "Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja." Tehnički vjesnik, vol. 21, br. 5, 2014, str. 1035-1040. https://hrcak.srce.hr/129050. Citirano 07.03.2021.
Chicago 17th Edition Mateša, Branko, Ivan Samardžić i Marko Dunđer. "Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja." Tehnički vjesnik 21, br. 5 (2014): 1035-1040. https://hrcak.srce.hr/129050
Harvard Mateša, B., Samardžić, I., i Dunđer, M. (2014). 'Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja', Tehnički vjesnik, 21(5), str. 1035-1040. Preuzeto s: https://hrcak.srce.hr/129050 (Datum pristupa: 07.03.2021.)
Vancouver Mateša B, Samardžić I, Dunđer M. Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja. Tehnički vjesnik [Internet]. 2014 [pristupljeno 07.03.2021.];21(5):1035-1040. Dostupno na: https://hrcak.srce.hr/129050
IEEE B. Mateša, I. Samardžić i M. Dunđer, "Utjecaj toplinske obradbe na slabljenje platiranog raznovrsnog spoja", Tehnički vjesnik, vol.21, br. 5, str. 1035-1040, 2014. [Online]. Dostupno na: https://hrcak.srce.hr/129050. [Citirano: 07.03.2021.]
Sažetak The dissimilar specimens (ASTM A387 Gr.12 + ASTM A240 TP 304L) clad by different procedures (explosion welding, submerged arc welding–surfacing using strip electrode (SAW) and hot rolling) were heat treated (650 °C through 2 hours). The shear strength testing of clad joints and Charpy impact energy testing were performed. The statistical analysis of testing results was elaborated, and the significance of heat treatment influences on the clad joints weakness was established.