A mechanism analysis of transverse weld cracks of marine thick steel plate

Haibo Wang ; (1) School of Materials Science and Engineering, Tianjin University, Weijin Rd, 92, Nankai, Tianjin 300072, China; (2) Tianjin Special Equipment Inspection Institute, Hangtian Street, Nankai, Tianjin 300192, China
Dongpo Wang ; School of Materials Science and Engineering, Tianjin University, Weijin Rd, 92, Nankai, Tianjin 300072, China
Fangjie Cheng ; School of Materials Science and Engineering, Tianjin University, Weijin Rd, 92, Nankai, Tianjin 300072, China
Ying Wang ; School of Materials Science and Engineering, Tianjin University, Weijin Rd, 92, Nankai, Tianjin 300072, China

Puni tekst: engleski, pdf (8 MB) str. 289-296 preuzimanja: 400* citiraj
APA 6th Edition
Wang, H., Wang, D., Cheng, F. i Wang, Y. (2015). A mechanism analysis of transverse weld cracks of marine thick steel plate. Tehnički vjesnik, 22 (2), 289-296. https://doi.org/10.17559/TV-20150310112039
MLA 8th Edition
Wang, Haibo, et al. "A mechanism analysis of transverse weld cracks of marine thick steel plate." Tehnički vjesnik, vol. 22, br. 2, 2015, str. 289-296. https://doi.org/10.17559/TV-20150310112039. Citirano 15.10.2019.
Chicago 17th Edition
Wang, Haibo, Dongpo Wang, Fangjie Cheng i Ying Wang. "A mechanism analysis of transverse weld cracks of marine thick steel plate." Tehnički vjesnik 22, br. 2 (2015): 289-296. https://doi.org/10.17559/TV-20150310112039
Harvard
Wang, H., et al. (2015). 'A mechanism analysis of transverse weld cracks of marine thick steel plate', Tehnički vjesnik, 22(2), str. 289-296. https://doi.org/10.17559/TV-20150310112039
Vancouver
Wang H, Wang D, Cheng F, Wang Y. A mechanism analysis of transverse weld cracks of marine thick steel plate. Tehnički vjesnik [Internet]. 2015 [pristupljeno 15.10.2019.];22(2):289-296. https://doi.org/10.17559/TV-20150310112039
IEEE
H. Wang, D. Wang, F. Cheng i Y. Wang, "A mechanism analysis of transverse weld cracks of marine thick steel plate", Tehnički vjesnik, vol.22, br. 2, str. 289-296, 2015. [Online]. https://doi.org/10.17559/TV-20150310112039
Puni tekst: hrvatski, pdf (8 MB) str. 289-296 preuzimanja: 179* citiraj
APA 6th Edition
Wang, H., Wang, D., Cheng, F. i Wang, Y. (2015). Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima. Tehnički vjesnik, 22 (2), 289-296. https://doi.org/10.17559/TV-20150310112039
MLA 8th Edition
Wang, Haibo, et al. "Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima." Tehnički vjesnik, vol. 22, br. 2, 2015, str. 289-296. https://doi.org/10.17559/TV-20150310112039. Citirano 15.10.2019.
Chicago 17th Edition
Wang, Haibo, Dongpo Wang, Fangjie Cheng i Ying Wang. "Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima." Tehnički vjesnik 22, br. 2 (2015): 289-296. https://doi.org/10.17559/TV-20150310112039
Harvard
Wang, H., et al. (2015). 'Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima', Tehnički vjesnik, 22(2), str. 289-296. https://doi.org/10.17559/TV-20150310112039
Vancouver
Wang H, Wang D, Cheng F, Wang Y. Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima. Tehnički vjesnik [Internet]. 2015 [pristupljeno 15.10.2019.];22(2):289-296. https://doi.org/10.17559/TV-20150310112039
IEEE
H. Wang, D. Wang, F. Cheng i Y. Wang, "Analiza mehanizma poprečnih lomova zavara brodskog debelog čeličnog lima", Tehnički vjesnik, vol.22, br. 2, str. 289-296, 2015. [Online]. https://doi.org/10.17559/TV-20150310112039

Sažetak
In the welding process of jackets for offshore platform, transverse weld cracks occur frequently, even when welding techniques, welding materials and marine steel plates used are stringently selected. But now defect failure analysis and mechanism study on this issue are scarce. To fully study the causes of transverse weld cracks of marine thick steel plate, this research uses instruments including metalloscope, scanning electron microscope (SEM), Energy Dispersive Spectrometer (EDS) and Auger Electronic Spectrom (AES). Researchers conclude that transverse weld cracks are welding hot cracks.

Ključne riječi
inclusions; thick steel plate; transverse weld cracks; welding hot cracks