Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes

Lihua Lv ; Green Applied Fiber Technology Institute, Dalian Polytechnic University, Dalian, China
Xinyue Wang ; School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, China
Yongling Yu ; School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, China
Jing Cui ; School of Textile and Material Engineering, Dalian Polytechnic University, Dalian, China

Puni tekst: engleski, pdf (495 KB) str. 95-99 preuzimanja: 147* citiraj
APA 6th Edition
Lv, L., Wang, X., Yu, Y. i Cui, J. (2014). Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes. Tekstil, 63 (3-4), 95-99. Preuzeto s https://hrcak.srce.hr/142481
MLA 8th Edition
Lv, Lihua, et al. "Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes." Tekstil, vol. 63, br. 3-4, 2014, str. 95-99. https://hrcak.srce.hr/142481. Citirano 24.11.2020.
Chicago 17th Edition
Lv, Lihua, Xinyue Wang, Yongling Yu i Jing Cui. "Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes." Tekstil 63, br. 3-4 (2014): 95-99. https://hrcak.srce.hr/142481
Harvard
Lv, L., et al. (2014). 'Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes', Tekstil, 63(3-4), str. 95-99. Preuzeto s: https://hrcak.srce.hr/142481 (Datum pristupa: 24.11.2020.)
Vancouver
Lv L, Wang X, Yu Y, Cui J. Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes. Tekstil [Internet]. 2014 [pristupljeno 24.11.2020.];63(3-4):95-99. Dostupno na: https://hrcak.srce.hr/142481
IEEE
L. Lv, X. Wang, Y. Yu i J. Cui, "Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes", Tekstil, vol.63, br. 3-4, str. 95-99, 2014. [Online]. Dostupno na: https://hrcak.srce.hr/142481. [Citirano: 24.11.2020.]
Puni tekst: hrvatski, pdf (738 KB) str. 89-94 preuzimanja: 196* citiraj
APA 6th Edition
Lv, L., Wang, X., Yu, Y. i Cui, J. (2014). Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana. Tekstil, 63 (3-4), 89-94. Preuzeto s https://hrcak.srce.hr/142481
MLA 8th Edition
Lv, Lihua, et al. "Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana." Tekstil, vol. 63, br. 3-4, 2014, str. 89-94. https://hrcak.srce.hr/142481. Citirano 24.11.2020.
Chicago 17th Edition
Lv, Lihua, Xinyue Wang, Yongling Yu i Jing Cui. "Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana." Tekstil 63, br. 3-4 (2014): 89-94. https://hrcak.srce.hr/142481
Harvard
Lv, L., et al. (2014). 'Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana', Tekstil, 63(3-4), str. 89-94. Preuzeto s: https://hrcak.srce.hr/142481 (Datum pristupa: 24.11.2020.)
Vancouver
Lv L, Wang X, Yu Y, Cui J. Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana. Tekstil [Internet]. 2014 [pristupljeno 24.11.2020.];63(3-4):89-94. Dostupno na: https://hrcak.srce.hr/142481
IEEE
L. Lv, X. Wang, Y. Yu i J. Cui, "Izrada i svojstva kompozita za zaštitu od gorenja od nezbrinutih ljusaka kikirikija, polipropilena i termoplastičnih poliuretana", Tekstil, vol.63, br. 3-4, str. 89-94, 2014. [Online]. Dostupno na: https://hrcak.srce.hr/142481. [Citirano: 24.11.2020.]

Sažetak
Fabrication and properties of flame retardant composites made of abandoned peanut hull, polypropylene and thermoplastic polyurethanes
Lihua Lv*1,2, Xinyue Wang*1,2, Yongling Yu*1,2, and Jing Cui*2
In order to make possible recycling agriculture waste and decrease the environment pollution caused by high polymer, flame retardant composites made of abandoned peanut hull as reinforced materials, abandoned PP (polypropylene) and abandoned TPU (thermoplastic polyurethanes) as matrix materials and magnesium hydroxide as flame retardant reagent were discussed in this article. And the mechanical properties and flame retardant properties of composites were tested and analyzed by orthogonal experiment and single factor analysis experiments. And the optimized processing conditions were concluded as follows: mass fraction of peanut hull 40 %, ratio of PP and TPU 3:1, hot pressing temperature 170 ℃, hot pressing pressure12 MPa, hot pressing time10 min, and plasticizing time 5 min. Under above conditions, properties of composites were as follow: density 1.12 g/cm3, tensile strength 23.85 MPa, bending strength 46.29 Mpa and impact energy absorption 10.19 kJ/m2. Besides, with magnesium hydroxide whose dosage was 100 % (compared to the matrix) being added under the optimized processing conditions, the mechanical properties and flame retardant properties of composites were as follow: LOI 29.7, density 1.27 g/cm3, tensile strength 10.37 MPa, bending strength 29.42 MPa and impact energy absorption 3.85 kJ/m2.

Ključne riječi
composites; ababdoned peanut hull; polypropylene; thermoplastic polyurethanes; mechanical properties; flame retardant properties