Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel

Ai-Qin Wang ; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China
Ming Li ; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China
Douqin Ma ; School of Physical Engineering, Zhengzhou University, 450 001 Zhengzhou, Henan, P.R. China
Qinjie Wu ; School of Physical Engineering, Zhengzhou University, 450 001 Zhengzhou, Henan, P.R. China
Jingpei Xie ; School of Materials Science and Engineering, Henan University of Science and Technology, 471 023 Luoyang, P.R. China

Puni tekst: engleski, pdf (856 KB) str. 11-16 preuzimanja: 378* citiraj
APA 6th Edition
Wang, A., Li, M., Ma, D., Wu, Q. i Xie, J. (2016). Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel. Kemija u industriji, 65 (1-2), 11-16. https://doi.org/10.15255/KUI.2015.047
MLA 8th Edition
Wang, Ai-Qin, et al. "Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel." Kemija u industriji, vol. 65, br. 1-2, 2016, str. 11-16. https://doi.org/10.15255/KUI.2015.047. Citirano 19.09.2020.
Chicago 17th Edition
Wang, Ai-Qin, Ming Li, Douqin Ma, Qinjie Wu i Jingpei Xie. "Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel." Kemija u industriji 65, br. 1-2 (2016): 11-16. https://doi.org/10.15255/KUI.2015.047
Harvard
Wang, A., et al. (2016). 'Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel', Kemija u industriji, 65(1-2), str. 11-16. https://doi.org/10.15255/KUI.2015.047
Vancouver
Wang A, Li M, Ma D, Wu Q, Xie J. Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel. Kemija u industriji [Internet]. 2016 [pristupljeno 19.09.2020.];65(1-2):11-16. https://doi.org/10.15255/KUI.2015.047
IEEE
A. Wang, M. Li, D. Ma, Q. Wu i J. Xie, "Effect of Lanthanum on Microstructures and Properties of ASTM A216 Steel", Kemija u industriji, vol.65, br. 1-2, str. 11-16, 2016. [Online]. https://doi.org/10.15255/KUI.2015.047

Sažetak
In order to satisfy the rudder horn casting standards of the International Association of Classification Societies, the properties of ASTM A216 steel should be improved. Therefore, in this article the rudder horn casting and accompanying specimens were cast moulded by arc furnace smelting, external refining, and modification treatment of the molten steel by lanthanum. The samples were first underwent normalizing treatment at 900 °C for 10 hours, then air cooled, followed by tempering treatment at 600 °C for 7 hours and samples were air cooled again. The mechanical properties and microstructures of the samples were measured. The crystallography relationships between lanthanum compounds formed in the molten steel and primary δ-Fe were analysed. The nucleation effect of lanthanum compounds as a heterogeneous nucleation core of primary δ-Fe were calculated and discussed based on two-dimensional mismatch theory. The results indicated that the strip MnS inclusions in ASTM A216 steel became granular rare earth compound inclusions due to La. The refined microstructures were obtained by a synergistic effect of the enhanced condensate depression and the nucleation rate of melt and La compounds as the heterogeneous nucleation caused by La.

Ključne riječi
ASTM A216 steel; inclusion; lanthanum; two-dimensional mismatch; grain refinement