Effect of electrolyte temperature on the thickness of anodic aluminium oxide (AAO) layer

P. Michal ; Institute of Technology and Businesses in České Budějovice, České Budějovice, Czech Republic
A. Vagaská ; Faculty of Manufacturing Technologies with a seat in Presov, Technical University of Kosice, Slovakia
E. Fechová ; Faculty of Manufacturing Technologies with a seat in Presov, Technical University of Kosice, Slovakia
M. Gombár ; Institute of Technology and Businesses in České Budějovice, České Budějovice, Czech Republic
D. Kozak ; Mechanical Engineering Faculty in Slavonski Brod, J. J. Strossmayer University of Osijek, Croatia


Puni tekst: engleski pdf 197 Kb

str. 403-406

preuzimanja: 2.469

citiraj


Sažetak

Effect of electrolyte temperature on the thickness of resulting oxide layer has been studied. Unlike previous published studies this article was aimed to monitor the relationship between electrolyte temperature and resulting AAO layer thickness in interaction with other input factors affecting during anodizing process under special process condition, i.e. lower concentration of sulphuric acid, oxalic acid, boric acid and sodium chloride. According to Design of Experiments (DOE) 80 individual test runs of experiment were carried out. Using statistical analysis and artificial intelligence for evaluation, the computational model predicting the thickness of oxide layer in the range from 5 / μm to 15 / μm with tolerance ± 0,5 / μm was developed.

Ključne riječi

anodic aluminium oxide (AAO); layer thickness; electrolyte; temperature; oxidation