The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al)

R. Mola ; Kielce University of Technology, Poland
S. Mróz ; Częstochowa University of Technology, Poland
P. Szota ; Częstochowa University of Technology, Poland
S. Sawicki ; Częstochowa University of Technology, Poland

Puni tekst: engleski, pdf (180 KB) str. 625-627 preuzimanja: 309* citiraj
APA 6th Edition
Mola, R., Mróz, S., Szota, P. i Sawicki, S. (2016). The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al). Metalurgija, 55 (4), 625-627. Preuzeto s https://hrcak.srce.hr/157382
MLA 8th Edition
Mola, R., et al. "The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al)." Metalurgija, vol. 55, br. 4, 2016, str. 625-627. https://hrcak.srce.hr/157382. Citirano 06.12.2019.
Chicago 17th Edition
Mola, R., S. Mróz, P. Szota i S. Sawicki. "The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al)." Metalurgija 55, br. 4 (2016): 625-627. https://hrcak.srce.hr/157382
Harvard
Mola, R., et al. (2016). 'The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al)', Metalurgija, 55(4), str. 625-627. Preuzeto s: https://hrcak.srce.hr/157382 (Datum pristupa: 06.12.2019.)
Vancouver
Mola R, Mróz S, Szota P, Sawicki S. The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al). Metalurgija [Internet]. 2016 [pristupljeno 06.12.2019.];55(4):625-627. Dostupno na: https://hrcak.srce.hr/157382
IEEE
R. Mola, S. Mróz, P. Szota i S. Sawicki, "The analysis of the plastic deformation of two-layered magnesium – aluminium alloys (AZ31 – Al)", Metalurgija, vol.55, br. 4, str. 625-627, 2016. [Online]. Dostupno na: https://hrcak.srce.hr/157382. [Citirano: 06.12.2019.]

Sažetak
The paper presents the results of physical modelling of the plastic deformation of the two-layered AZ31 - Al alloys. The AZ31 - Al feedstock was produced using the diffusion bonding method. Heating under pressure led to the formation of a continuous layer of the intermetallic phases at the bond interface of AZ31 - Al. A compression test was used to determine the plastic deformation of the two-layered AZ31 - Al alloys. Based on the analysis of the investigation results it has been found that, as the strain rate decreases and temperature increases, the intermetallic phase yields, and a distinct thinning of the intermetallic phase layer has occurred in the zone directly affected by the anvil.

Ključne riječi
magnesium – aluminium alloys; microstructure; plastic deformation; diffusion bonding; physical modelling