hrcak mascot   Srce   HID

Prethodno priopćenje

Influence of induction hardening parameters on the GS30Mn5 weld properties

V. Marušić ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
I. Samardžić ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
I. Opačak ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
L. Marušić ; Technical Department of the College of Slavonski Brod, Croatia

Puni tekst: engleski, pdf (224 KB) str. 730-732 preuzimanja: 722* citiraj
APA 6th Edition
Marušić, V., Samardžić, I., Opačak, I. i Marušić, L. (2016). Influence of induction hardening parameters on the GS30Mn5 weld properties. Metalurgija, 55 (4), 730-732. Preuzeto s https://hrcak.srce.hr/157436
MLA 8th Edition
Marušić, V., et al. "Influence of induction hardening parameters on the GS30Mn5 weld properties." Metalurgija, vol. 55, br. 4, 2016, str. 730-732. https://hrcak.srce.hr/157436. Citirano 27.01.2020.
Chicago 17th Edition
Marušić, V., I. Samardžić, I. Opačak i L. Marušić. "Influence of induction hardening parameters on the GS30Mn5 weld properties." Metalurgija 55, br. 4 (2016): 730-732. https://hrcak.srce.hr/157436
Harvard
Marušić, V., et al. (2016). 'Influence of induction hardening parameters on the GS30Mn5 weld properties', Metalurgija, 55(4), str. 730-732. Preuzeto s: https://hrcak.srce.hr/157436 (Datum pristupa: 27.01.2020.)
Vancouver
Marušić V, Samardžić I, Opačak I, Marušić L. Influence of induction hardening parameters on the GS30Mn5 weld properties. Metalurgija [Internet]. 2016 [pristupljeno 27.01.2020.];55(4):730-732. Dostupno na: https://hrcak.srce.hr/157436
IEEE
V. Marušić, I. Samardžić, I. Opačak i L. Marušić, "Influence of induction hardening parameters on the GS30Mn5 weld properties", Metalurgija, vol.55, br. 4, str. 730-732, 2016. [Online]. Dostupno na: https://hrcak.srce.hr/157436. [Citirano: 27.01.2020.]

Sažetak
This study examines parameters of post-weld heat treatment on the test specimens made of cast steel GS30Mn5. The welding is performed with shielded metal arc welding (SMAW) process. The aim is to obtain the surface without illicit cracks, with hardness ranging from 320 up to 400 HB. After induction heating, the specimens are cooled alternately with air and water. Decreased speed of quenching results in avoiding the occurrence of illicit splashes, while the hardness is maintained within the prescribed limits.

Ključne riječi
welding; GS30Mn5; post weld heat treatment; mechanical properties; structure