HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method

Jerzy Jozwik ; Mechanical Engineering Faculty, Lublin University of Technology, Nadbystrzycka Street, 36, 20-618 Lublin, Poland
Krzysztof Dziedzic ; Mechanical Engineering Faculty, Lublin University of Technology, Nadbystrzycka Street, 36, 20-618 Lublin, Poland
Ireneusz Usydus ; The Institute of Technical Sciences and Aviation, The State School of Higher Education, Pocztowa Street, 54, 22-100 Chelm, Poland
Pero Raos   ORCID icon orcid.org/0000-0001-9263-1325 ; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić-Mažuranić 2, 35000 Slavonski Brod, Croatia
Grzegorz M. Krolczyk ; Opole University of Technology, 76 Prószkowska Street, 45-758 Opole, Poland

Puni tekst: engleski, pdf (2 MB) str. 1405-1409 preuzimanja: 218* citiraj
APA 6th Edition
Jozwik, J., Dziedzic, K., Usydus, I., Raos, P. i Krolczyk, G.M. (2016). HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method. Tehnički vjesnik, 23 (5), 1405-1409. https://doi.org/10.17559/TV-20150402150811
MLA 8th Edition
Jozwik, Jerzy, et al. "HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method." Tehnički vjesnik, vol. 23, br. 5, 2016, str. 1405-1409. https://doi.org/10.17559/TV-20150402150811. Citirano 27.02.2021.
Chicago 17th Edition
Jozwik, Jerzy, Krzysztof Dziedzic, Ireneusz Usydus, Pero Raos i Grzegorz M. Krolczyk. "HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method." Tehnički vjesnik 23, br. 5 (2016): 1405-1409. https://doi.org/10.17559/TV-20150402150811
Harvard
Jozwik, J., et al. (2016). 'HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method', Tehnički vjesnik, 23(5), str. 1405-1409. https://doi.org/10.17559/TV-20150402150811
Vancouver
Jozwik J, Dziedzic K, Usydus I, Raos P, Krolczyk GM. HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method. Tehnički vjesnik [Internet]. 2016 [pristupljeno 27.02.2021.];23(5):1405-1409. https://doi.org/10.17559/TV-20150402150811
IEEE
J. Jozwik, K. Dziedzic, I. Usydus, P. Raos i G.M. Krolczyk, "HS 6-5-2 steel surface layer development in carbonitriding with ZeroFlow method", Tehnički vjesnik, vol.23, br. 5, str. 1405-1409, 2016. [Online]. https://doi.org/10.17559/TV-20150402150811
Puni tekst: hrvatski, pdf (2 MB) str. 1405-1409 preuzimanja: 200* citiraj
APA 6th Edition
Jozwik, J., Dziedzic, K., Usydus, I., Raos, P. i Krolczyk, G.M. (2016). Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow. Tehnički vjesnik, 23 (5), 1405-1409. https://doi.org/10.17559/TV-20150402150811
MLA 8th Edition
Jozwik, Jerzy, et al. "Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow." Tehnički vjesnik, vol. 23, br. 5, 2016, str. 1405-1409. https://doi.org/10.17559/TV-20150402150811. Citirano 27.02.2021.
Chicago 17th Edition
Jozwik, Jerzy, Krzysztof Dziedzic, Ireneusz Usydus, Pero Raos i Grzegorz M. Krolczyk. "Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow." Tehnički vjesnik 23, br. 5 (2016): 1405-1409. https://doi.org/10.17559/TV-20150402150811
Harvard
Jozwik, J., et al. (2016). 'Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow', Tehnički vjesnik, 23(5), str. 1405-1409. https://doi.org/10.17559/TV-20150402150811
Vancouver
Jozwik J, Dziedzic K, Usydus I, Raos P, Krolczyk GM. Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow. Tehnički vjesnik [Internet]. 2016 [pristupljeno 27.02.2021.];23(5):1405-1409. https://doi.org/10.17559/TV-20150402150811
IEEE
J. Jozwik, K. Dziedzic, I. Usydus, P. Raos i G.M. Krolczyk, "Dobivanje površinskog sloja HS 6-5-2 čelika karbonitriranjem uz primjenu metode ZeroFlow", Tehnički vjesnik, vol.23, br. 5, str. 1405-1409, 2016. [Online]. https://doi.org/10.17559/TV-20150402150811

Sažetak
The paper reviews the process of surface layer development with the use of carbonitriding and carbonitriding with oxidation. Employed for that purpose was a modern and ecological method called ZeroFlow. Research was carried out using HS 6-5-2 steel. Single-component nitrifying atmosphere of ammonia NH3 was applied. The temperature of the processes was 570 °C. Diffusion layers were obtained on the steel. The thickness of the layers achieved during the microstructural research equalled from about 125 μm after carbonitriding with oxidation to about 187 μm after carbonitriding. Surface hardness HV1 was the highest for the carbonitrided layer - 1027 HV1, whereas in the case of carbonitriding with oxidation it amounted to 1018 HV1. As far as surface hardness HV30 is concerned, it was at the level of 813 HV30 for the carbonitrided layer and 795 HV30 for carbonitriding with oxidation. Surface hardness test results indicate surface layer hardening.

Ključne riječi
carbonitriding; microhardness; nitriding; oxidation; surface layer