The effect of high-frequencies loading on the fatigue cracking of nodular cast iron

R. Ulewicz ; Czestochowa University of Technology, Czestochowa, Poland
P. Tomski ; Czestochowa University of Technology, Czestochowa, Poland

Puni tekst: engleski, pdf (430 KB) str. 33-36 preuzimanja: 316* citiraj
APA 6th Edition
Ulewicz, R. i Tomski, P. (2017). The effect of high-frequencies loading on the fatigue cracking of nodular cast iron. Metalurgija, 56 (1-2), 33-36. Preuzeto s https://hrcak.srce.hr/168847
MLA 8th Edition
Ulewicz, R. i P. Tomski. "The effect of high-frequencies loading on the fatigue cracking of nodular cast iron." Metalurgija, vol. 56, br. 1-2, 2017, str. 33-36. https://hrcak.srce.hr/168847. Citirano 27.01.2020.
Chicago 17th Edition
Ulewicz, R. i P. Tomski. "The effect of high-frequencies loading on the fatigue cracking of nodular cast iron." Metalurgija 56, br. 1-2 (2017): 33-36. https://hrcak.srce.hr/168847
Harvard
Ulewicz, R., i Tomski, P. (2017). 'The effect of high-frequencies loading on the fatigue cracking of nodular cast iron', Metalurgija, 56(1-2), str. 33-36. Preuzeto s: https://hrcak.srce.hr/168847 (Datum pristupa: 27.01.2020.)
Vancouver
Ulewicz R, Tomski P. The effect of high-frequencies loading on the fatigue cracking of nodular cast iron. Metalurgija [Internet]. 2017 [pristupljeno 27.01.2020.];56(1-2):33-36. Dostupno na: https://hrcak.srce.hr/168847
IEEE
R. Ulewicz i P. Tomski, "The effect of high-frequencies loading on the fatigue cracking of nodular cast iron", Metalurgija, vol.56, br. 1-2, str. 33-36, 2017. [Online]. Dostupno na: https://hrcak.srce.hr/168847. [Citirano: 27.01.2020.]

Sažetak
The article presents the results of fatigue tests using high-frequency loading of nodular cast iron. Nodular cast iron GJS-500-7, GJS-600-3 and cast iron ADI with a tensile strength of Rm = 1 125 MPa were used for the tests. The fatigue tests were conducted on a resonance testing machine. For the cast iron grades under investigation, fatigue characteristics in high and ultra-high-cycle regions were experimentally determined. After the completion of the tests, the fractographic analysis of fatigue fractures was made with the aim of determining the fatigue crack initiation location and the fracture mechanism.

Ključne riječi
nodular cast iron; fatigue failure; high frequency fatigue testing; fractography