Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill

A. Mashekova ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan
A. Turdaliev ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan
A. Kawalek ; Czestochowa University of Technology, Czestochowa, Poland
S. Mashekov ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan
U. Murzakhmetova ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan
L. Kurmangaliyeva ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan
N. Smagulova ; Institute of Industrial Engineering, Kazakh National Research Technical University after K. Satpayev, Almaty, Kazakhstan

Puni tekst: engleski, pdf (327 KB) str. 119-122 preuzimanja: 170* citiraj
APA 6th Edition
Mashekova, A., Turdaliev, A., Kawalek, A., Mashekov, S., Murzakhmetova, U., Kurmangaliyeva, L. i Smagulova, N. (2017). Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill. Metalurgija, 56 (1-2), 119-122. Preuzeto s https://hrcak.srce.hr/168903
MLA 8th Edition
Mashekova, A., et al. "Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill." Metalurgija, vol. 56, br. 1-2, 2017, str. 119-122. https://hrcak.srce.hr/168903. Citirano 20.01.2020.
Chicago 17th Edition
Mashekova, A., A. Turdaliev, A. Kawalek, S. Mashekov, U. Murzakhmetova, L. Kurmangaliyeva i N. Smagulova. "Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill." Metalurgija 56, br. 1-2 (2017): 119-122. https://hrcak.srce.hr/168903
Harvard
Mashekova, A., et al. (2017). 'Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill', Metalurgija, 56(1-2), str. 119-122. Preuzeto s: https://hrcak.srce.hr/168903 (Datum pristupa: 20.01.2020.)
Vancouver
Mashekova A, Turdaliev A, Kawalek A, Mashekov S, Murzakhmetova U, Kurmangaliyeva L i sur. Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill. Metalurgija [Internet]. 2017 [pristupljeno 20.01.2020.];56(1-2):119-122. Dostupno na: https://hrcak.srce.hr/168903
IEEE
A. Mashekova, et al., "Ultrafinegrained structure of D16 aluminium alloy after rolling in the corrugated rolls and on the longitudinal-wedge mill", Metalurgija, vol.56, br. 1-2, str. 119-122, 2017. [Online]. Dostupno na: https://hrcak.srce.hr/168903. [Citirano: 20.01.2020.]

Sažetak
The article explains the influence of number of passes on the parameters of the microstructure of D16 aluminium alloy during rolling in the corrugated rolls, and the impact of the drafts while rolling of the strips on the longitudinal wedge mill. A comparative evaluation of the grain size of the ultrafine grained structure was conducted after rolling strips in the corrugated rolls by various passes, and after rolling on the longitudinal wedge mill at deformation temperature of 320 °C. It is shown that the sheet material of D16 aluminium alloy ensures uniform formation of an ultrafine grain structure with the size of about 220 - 240 nm, which leads to increased strength properties of the alloy and preserve good ductility.

Ključne riječi
aluminium; rolling, strip; severe plastic deformation; ultrafine grained structure