The influence of drawing speed on surface topography of high carbon steel wires

M. Suliga ; Faculty of Production Engineering and Materials Technology, Czestochowa University of Technology, Poland

Puni tekst: engleski, pdf (189 KB) str. 182-184 preuzimanja: 423* citiraj
APA 6th Edition
Suliga, M. (2017). The influence of drawing speed on surface topography of high carbon steel wires. Metalurgija, 56 (1-2), 182-184. Preuzeto s https://hrcak.srce.hr/168926
MLA 8th Edition
Suliga, M.. "The influence of drawing speed on surface topography of high carbon steel wires." Metalurgija, vol. 56, br. 1-2, 2017, str. 182-184. https://hrcak.srce.hr/168926. Citirano 26.01.2020.
Chicago 17th Edition
Suliga, M.. "The influence of drawing speed on surface topography of high carbon steel wires." Metalurgija 56, br. 1-2 (2017): 182-184. https://hrcak.srce.hr/168926
Harvard
Suliga, M. (2017). 'The influence of drawing speed on surface topography of high carbon steel wires', Metalurgija, 56(1-2), str. 182-184. Preuzeto s: https://hrcak.srce.hr/168926 (Datum pristupa: 26.01.2020.)
Vancouver
Suliga M. The influence of drawing speed on surface topography of high carbon steel wires. Metalurgija [Internet]. 2017 [pristupljeno 26.01.2020.];56(1-2):182-184. Dostupno na: https://hrcak.srce.hr/168926
IEEE
M. Suliga, "The influence of drawing speed on surface topography of high carbon steel wires", Metalurgija, vol.56, br. 1-2, str. 182-184, 2017. [Online]. Dostupno na: https://hrcak.srce.hr/168926. [Citirano: 26.01.2020.]

Sažetak
In this work the influence of the drawing speed on surface topography of high carbon steel wires has been assessed. The drawing process of f 5,5 mm wire rod to the final wire of f 1,7 mm was conducted in 12 passes by means of a modern Koch multi-die drawing machine. The drawing speeds in the last passes were: 5, 10, 15, 20 and 25 m/s. For final wires f 1,7 mm the three-dimensional analysis of the wire surface topography investigation was determined. It has been proved that the wire topography in the drawing process is characterized by a random anisotropy and the amount of directing the geometrical structure of the surface depends on the drawing speed.

Ključne riječi
high carbon steel; drawing; wire rod; speed; surface topography