High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment

T. Pornpibunsompop   ORCID icon orcid.org/0000-0002-2271-742X ; Division of Materials Technology, School of Energy, Environment and Materials, King Mongkut’s University of Technology Thonburi, Thailand
P. Thanakijkasem ; Division of Materials Technology, School of Energy, Environment and Materials, King Mongkut’s University of Technology Thonburi, Thailand

Puni tekst: engleski, pdf (344 KB) str. 83-86 preuzimanja: 627* citiraj
APA 6th Edition
Pornpibunsompop, T. i Thanakijkasem, P. (2018). High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment. Metalurgija, 57 (1-2), 83-86. Preuzeto s https://hrcak.srce.hr/189370
MLA 8th Edition
Pornpibunsompop, T. i P. Thanakijkasem. "High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment." Metalurgija, vol. 57, br. 1-2, 2018, str. 83-86. https://hrcak.srce.hr/189370. Citirano 21.01.2020.
Chicago 17th Edition
Pornpibunsompop, T. i P. Thanakijkasem. "High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment." Metalurgija 57, br. 1-2 (2018): 83-86. https://hrcak.srce.hr/189370
Harvard
Pornpibunsompop, T., i Thanakijkasem, P. (2018). 'High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment', Metalurgija, 57(1-2), str. 83-86. Preuzeto s: https://hrcak.srce.hr/189370 (Datum pristupa: 21.01.2020.)
Vancouver
Pornpibunsompop T, Thanakijkasem P. High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment. Metalurgija [Internet]. 2018 [pristupljeno 21.01.2020.];57(1-2):83-86. Dostupno na: https://hrcak.srce.hr/189370
IEEE
T. Pornpibunsompop i P. Thanakijkasem, "High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment", Metalurgija, vol.57, br. 1-2, str. 83-86, 2018. [Online]. Dostupno na: https://hrcak.srce.hr/189370. [Citirano: 21.01.2020.]

Sažetak
High temperature corrosion and stress corrosion cracking of 310S austenitic stainless steel in wet chloride environment at a high temperature was investigated. The result showed that high temperature corrosion products mostly consisted of ferrous oxides and chromium oxides. Chloride ions attacked a chromium passive film and strongly reacted with iron and chromium. As a result of metal chlorides being volatized, tunnel of pores inside corrosion layer existed. Intergranular stress corrosion cracking was observed. The oxide originated on surface could act as a crack initiator and a crack propagation would progress along grain boundaries and particularly along tunnel of pores.

Ključne riječi
high temperature corrosion; stress corrosion cracking; austenitic stainless steel; chloride environment; x-ray methods