Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring
B. S. Sun
; Faculty of Mechanical Engineering & Mechanics, Ningbo University, China
C. W. Wang
; Faculty of Mechanical Engineering & Mechanics, Ningbo University, China
Z. L. Zhao
; Faculty of Mechanical Engineering & Mechanics, Ningbo University, China
APA 6th Edition Sun, B.S., Wang, C.W. i Zhao, Z.L. (2018). Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring. Metalurgija, 57 (4), 283-286. Preuzeto s https://hrcak.srce.hr/201742
MLA 8th Edition Sun, B. S., et al. "Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring." Metalurgija, vol. 57, br. 4, 2018, str. 283-286. https://hrcak.srce.hr/201742. Citirano 23.01.2021.
Chicago 17th Edition Sun, B. S., C. W. Wang i Z. L. Zhao. "Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring." Metalurgija 57, br. 4 (2018): 283-286. https://hrcak.srce.hr/201742
Harvard Sun, B.S., Wang, C.W., i Zhao, Z.L. (2018). 'Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring', Metalurgija, 57(4), str. 283-286. Preuzeto s: https://hrcak.srce.hr/201742 (Datum pristupa: 23.01.2021.)
Vancouver Sun BS, Wang CW, Zhao ZL. Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring. Metalurgija [Internet]. 2018 [pristupljeno 23.01.2021.];57(4):283-286. Dostupno na: https://hrcak.srce.hr/201742
IEEE B.S. Sun, C.W. Wang i Z.L. Zhao, "Research on cold rolling of 41Cr4/20NiCrMo7 bimetal composite bearing ring", Metalurgija, vol.57, br. 4, str. 283-286, 2018. [Online]. Dostupno na: https://hrcak.srce.hr/201742. [Citirano: 23.01.2021.]
Sažetak In order to improve the service life of bearing rings, a new method of cold rolling bimetal composite bearing rings was proposed in this paper.With Abaqus software,a finite element simulation model of the cold rolling of bimetal composite bearing rings was established. The law of the radial stress distribution, the diameter growth and the deformation of plastic zone during the cold rolling of bimetal composite bearing rings were analyzed. The results of these analyzes are helpful to study the deformation characteristics of the cold rolling of bimetal composite bearing rings. The results show that the bimetal composite bearing ring interface is well bonded and no segregation occurs during the process of cold rolling.