Metalurgija, Vol. 57 No. 4, 2018.

Izvorni znanstveni članak

Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere

S. A. A. Sajadi ; Sharif University of Technology, Institute of Water & Energy, Tehran, Iran
A. Nazari Alavi ; Sharif University of Technology, Institute of Water & Energy, Tehran, Iran
M. Mirzai ; Sharif University of Technology, Institute of Water & Energy, Tehran, Iran

Puni tekst: engleski, pdf (201 KB) str. 287-290 preuzimanja: 110* citiraj
APA 6th Edition
Sajadi, S.A.A., Nazari Alavi, A. i Mirzai, M. (2018). Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere. Metalurgija, 57 (4), 287-290. Preuzeto s https://hrcak.srce.hr/201743
MLA 8th Edition
Sajadi, S. A. A., et al. "Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere." Metalurgija, vol. 57, br. 4, 2018, str. 287-290. https://hrcak.srce.hr/201743. Citirano 14.12.2019.
Chicago 17th Edition
Sajadi, S. A. A., A. Nazari Alavi i M. Mirzai. "Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere." Metalurgija 57, br. 4 (2018): 287-290. https://hrcak.srce.hr/201743
Harvard
Sajadi, S.A.A., Nazari Alavi, A., i Mirzai, M. (2018). 'Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere', Metalurgija, 57(4), str. 287-290. Preuzeto s: https://hrcak.srce.hr/201743 (Datum pristupa: 14.12.2019.)
Vancouver
Sajadi SAA, Nazari Alavi A, Mirzai M. Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere. Metalurgija [Internet]. 2018 [pristupljeno 14.12.2019.];57(4):287-290. Dostupno na: https://hrcak.srce.hr/201743
IEEE
S.A.A. Sajadi, A. Nazari Alavi i M. Mirzai, "Investigation of thermal behavior of α-PbO and β-PbO in O2 atmosphere", Metalurgija, vol.57, br. 4, str. 287-290, 2018. [Online]. Dostupno na: https://hrcak.srce.hr/201743. [Citirano: 14.12.2019.]

Sažetak
The compounds α-lead oxide (α-PbO) and β-lead oxide (β-PbO) were purchased from Merck co. and used for thermal investigations in laboratory. The compound was heated in a thermogravimeter at different temperature, from 25 to 400 °C. The used gas atmosphere was O2. The received products were investigated by X-ray diffraction (XRD) technique. The received product Pb3O4 was confirmed by XRD. The textures of two different morphologies of α-PbO, β-PbO and the product Pb3O4 is investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM) techniques.

Ključne riječi
lead (II) oxide; Pb3O4; thermal analysis; thermogravimetry; SEM-TEM

Hrčak ID: 201743