Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood

Ayhan Ozcifci ; Faculty of Engineering, Aksaray University, Aksaray, Turkey
Erkan Kokten ; Faculty of Engineering, Karabuk University, Karabuk, Turkey
Nadir Ayrilmis ; Faculty of Forestry, Istanbul University, Istanbul, Turkey
Günay Özbay ; Faculty of Engineering, Aksaray University, Aksaray, Turkey
Suat Suat Altun ; Faculty of Engineering, Karabuk University, Karabuk, Turkey

Puni tekst: engleski, pdf (505 KB) str. 207-213 preuzimanja: 168* citiraj
APA 6th Edition
Ozcifci, A., Kokten, E., Ayrilmis, N., Özbay, G. i Suat Altun, S. (2018). Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood. Drvna industrija, 69 (3), 207-213. https://doi.org/10.5552/drind.2018.1717
MLA 8th Edition
Ozcifci, Ayhan, et al. "Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood." Drvna industrija, vol. 69, br. 3, 2018, str. 207-213. https://doi.org/10.5552/drind.2018.1717. Citirano 13.11.2019.
Chicago 17th Edition
Ozcifci, Ayhan, Erkan Kokten, Nadir Ayrilmis, Günay Özbay i Suat Suat Altun. "Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood." Drvna industrija 69, br. 3 (2018): 207-213. https://doi.org/10.5552/drind.2018.1717
Harvard
Ozcifci, A., et al. (2018). 'Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood', Drvna industrija, 69(3), str. 207-213. https://doi.org/10.5552/drind.2018.1717
Vancouver
Ozcifci A, Kokten E, Ayrilmis N, Özbay G, Suat Altun S. Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood. Drvna industrija [Internet]. 2018 [pristupljeno 13.11.2019.];69(3):207-213. https://doi.org/10.5552/drind.2018.1717
IEEE
A. Ozcifci, E. Kokten, N. Ayrilmis, G. Özbay i S. Suat Altun, "Effects of Catalysts on Modulus of Rupture and Chemical Structure of Heat– Treated Wood", Drvna industrija, vol.69, br. 3, str. 207-213, 2018. [Online]. https://doi.org/10.5552/drind.2018.1717

Sažetak
Heat treatment process, which is widely used in the wood industry, has shown some negative effects on the mechanical strength of wood. The objective of this study was to investigate the effects of catalysts on the modulus of rupture (MOR), mass loss and chemical structure of heat–treated Scotch pine (Pinus sylvestris L.) samples. For this purpose, some catalysts (50 % NaOH and 47 % KOH solutions, solid KOH) were added to the heat treatment process. Heat treatment experiments were performed under the nitrogen atmosphere at the temperature of 212 °C for 2 h. The MOR and chemical changes monitored by FT-IR spectra were then examined for the test groups. According to the results of this study, the use of commercial solid potassium hydroxide (KOH) in heat treatment decreased the degree of strength loss and mass loss of heat-treated wood. The strength (MOR) loss of samples heat-treated in the presence of potassium hydroxide was found to be only 5.4 %, while the strength loss in non-catalytic treatment was found to be 12.5 %.

Ključne riječi
heat treatment; Scotch pine; mechanical strength; catalyst; chemical properties