The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive

Timuçin Bardak   ORCID icon orcid.org/0000-0002-1403-1049 ; Department of Furniture and Decoration, Vocational Schools, Bartin University, Turkey
Eser Sozen   ORCID icon orcid.org/0000-0003-4798-7124 ; Department of Forest Industrial Engineering, Faculty of Forestry, Bartin University, Turkey
Kadir Kayahan ; Department of Furniture and Decoration, Vocational Schools, Bartin University, Turkey
Selahattin Bardak ; Department of Industrial Engineering, Faculty of Engineering and Architecture, Sinop University, Turkey

Puni tekst: engleski, pdf (546 KB) str. 247-252 preuzimanja: 214* citiraj
APA 6th Edition
Bardak, T., Sozen, E., Kayahan, K. i Bardak, S. (2018). The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive. Drvna industrija, 69 (3), 247-252. https://doi.org/10.5552/drind.2018.1755
MLA 8th Edition
Bardak, Timuçin, et al. "The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive." Drvna industrija, vol. 69, br. 3, 2018, str. 247-252. https://doi.org/10.5552/drind.2018.1755. Citirano 18.11.2019.
Chicago 17th Edition
Bardak, Timuçin, Eser Sozen, Kadir Kayahan i Selahattin Bardak. "The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive." Drvna industrija 69, br. 3 (2018): 247-252. https://doi.org/10.5552/drind.2018.1755
Harvard
Bardak, T., et al. (2018). 'The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive', Drvna industrija, 69(3), str. 247-252. https://doi.org/10.5552/drind.2018.1755
Vancouver
Bardak T, Sozen E, Kayahan K, Bardak S. The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive. Drvna industrija [Internet]. 2018 [pristupljeno 18.11.2019.];69(3):247-252. https://doi.org/10.5552/drind.2018.1755
IEEE
T. Bardak, E. Sozen, K. Kayahan i S. Bardak, "The Impact of Nanoparticles and Moisture Content on Bonding Strength of Urea Formaldehyde Resin Adhesive", Drvna industrija, vol.69, br. 3, str. 247-252, 2018. [Online]. https://doi.org/10.5552/drind.2018.1755

Sažetak
Wood and wood products have been used in different environmental conditions. Moisture content (MC) and relative humidity (RH) are key parameters for these conditions and bonding strength. Nanotechnology has paved the way to more durable adhesives. An experimental study was conducted to examine the effects of various nanoparticles and moisture content on bonding strength of urea formaldehyde (UF) resin adhesive. In this study, nanosilicon dioxide (SiO2) and titanium dioxide (TiO2) were blended with UF. Nanoparticle reinforced adhesives were processed at different nano fillers concentrations (0.5 % and 1 %) and each adhesive was tested at the moisture content of 0 %, 12 %, 18 % and 25 %. According to the results of bonding strength tests, contained nano-SiO2 adhesives showed better bonding strengths as compared to the control (pure UF) and contained nano-TiO2 adhesives. The highest bonding strength has been determined at 12 % wood moisture in all specimens. Increasing the moisture content has decreased bonding strength of all samples including control samples. This study showed that nano (SiO2 and TiO2) particles have improved the bonding strength of pure UF. Besides, the addition of nano-SiO2 and nano-TiO2 changed the physicochemical properties of UF adhesive by XRD test. The novelty of this study was to demonstrate that nanoparticles (SiO2 and TiO2)could be benefi cial for the bonding strength of UF adhesive in harsh environmental conditions.

Ključne riječi
nanoparticles; urea formaldehyde; moisture content; lap joint shear strength; bonding strength