Failure analysis of a diesel engine crankshaft

A. Y. Jiao   ORCID icon orcid.org/0000-0003-3606-5589 ; School of applied technology, University of Science and Technology Liaoning, Anshan, China
F. L. Chen ; School of mechanical Engineering and automation, University of Science and Technology Liaoning, Anshan, China
B. H. Liu ; School of mechanical Engineering and automation, University of Science and Technology Liaoning, Anshan, China
J. W. Deng ; Tianrun Crankshaft Co., Ltd., Wen deng, China

Puni tekst: engleski, pdf (419 KB) str. 113-116 preuzimanja: 16* citiraj
APA 6th Edition
Jiao, A.Y., Chen, F.L., Liu, B.H. i Deng, J.W. (2020). Failure analysis of a diesel engine crankshaft. Metalurgija, 59 (1), 113-116. Preuzeto s https://hrcak.srce.hr/224780
MLA 8th Edition
Jiao, A. Y., et al. "Failure analysis of a diesel engine crankshaft." Metalurgija, vol. 59, br. 1, 2020, str. 113-116. https://hrcak.srce.hr/224780. Citirano 14.10.2019.
Chicago 17th Edition
Jiao, A. Y., F. L. Chen, B. H. Liu i J. W. Deng. "Failure analysis of a diesel engine crankshaft." Metalurgija 59, br. 1 (2020): 113-116. https://hrcak.srce.hr/224780
Harvard
Jiao, A.Y., et al. (2020). 'Failure analysis of a diesel engine crankshaft', Metalurgija, 59(1), str. 113-116. Preuzeto s: https://hrcak.srce.hr/224780 (Datum pristupa: 14.10.2019.)
Vancouver
Jiao AY, Chen FL, Liu BH, Deng JW. Failure analysis of a diesel engine crankshaft. Metalurgija [Internet]. 2020 [pristupljeno 14.10.2019.];59(1):113-116. Dostupno na: https://hrcak.srce.hr/224780
IEEE
A.Y. Jiao, F.L. Chen, B.H. Liu i J.W. Deng, "Failure analysis of a diesel engine crankshaft", Metalurgija, vol.59, br. 1, str. 113-116, 2020. [Online]. Dostupno na: https://hrcak.srce.hr/224780. [Citirano: 14.10.2019.]

Sažetak
In this paper, the macroscopic observation and chemical composition analysis of the third crankshaft journal have been carried out. Moreover, macroscopic observation, chemical composition analysis and metallographic analysis were carried out, and were compared with the journal with cracks and without cracks. Based on the experimental results and the causes of crankshaft neck cracks, it can be concluded that the crack form of crankshaft goes along with the grain brittle direction.

Ključne riječi
42CrMo; crankshaft; crack; metallography; hardness