Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering

Mariusz L. Mamiński ; Warsaw University of Life Sciences, Faculty of Wood Technology, Warsaw, Poland
Anna Romanowska ; Warsaw University of Life Sciences, Faculty of Wood Technology, Warsaw, Poland

Puni tekst: engleski, pdf (494 KB) str. 229-233 preuzimanja: 273* citiraj
APA 6th Edition
Mamiński, M.L. i Romanowska, A. (2019). Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering. Drvna industrija, 70 (3), 229-233. https://doi.org/10.5552/drvind.2019.1830
MLA 8th Edition
Mamiński, Mariusz L. i Anna Romanowska. "Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering." Drvna industrija, vol. 70, br. 3, 2019, str. 229-233. https://doi.org/10.5552/drvind.2019.1830. Citirano 18.06.2021.
Chicago 17th Edition
Mamiński, Mariusz L. i Anna Romanowska. "Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering." Drvna industrija 70, br. 3 (2019): 229-233. https://doi.org/10.5552/drvind.2019.1830
Harvard
Mamiński, M.L., i Romanowska, A. (2019). 'Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering', Drvna industrija, 70(3), str. 229-233. https://doi.org/10.5552/drvind.2019.1830
Vancouver
Mamiński ML, Romanowska A. Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering. Drvna industrija [Internet]. 2019 [pristupljeno 18.06.2021.];70(3):229-233. https://doi.org/10.5552/drvind.2019.1830
IEEE
M.L. Mamiński i A. Romanowska, "Polyglycerol- and Sucrosebased Green Polyurethane Adhesives for Veneering", Drvna industrija, vol.70, br. 3, str. 229-233, 2019. [Online]. https://doi.org/10.5552/drvind.2019.1830

Sažetak
Veneering of particleboard with ABS foil and natural oak veneer was performed using polyglycerol- and sucrose-based polyurethane adhesives. Bonding strength between veneer and underlying board was determined according to EN 312 standard. Developed adhesive formulations exhibited bonding strengths between coating material and underlying board exceeding the surface soundness of particleboard (cohesive failure between 50 % and 100 %). Higher adhesion was found for natural oak veneers. Reactivity of the studied adhesives was comparable to those for commercial adhesives used in furniture industry. It has been demonstrated that biobased polyols can be considered environmentally benign and efficient components of polyurethane adhesives for furniture industry.

Ključne riječi
polyglycerol; polyol; polyurethane; sucrose; veneering