Influence of shot peening on surface properties and corrosion resistance of implant material AISI 316L

P. T. Iswanto ; Department of Mechanical and Industrial Engineering, Universitas Gadjah Mada, Yogyakarta, Indonesia
R. I. Yaqin ; Department of Mechanical and Industrial Engineering, Universitas Gadjah Mada, Yogyakarta, Indonesia
Akhyar ; Department of Mechanical Engineering and Industrial Engineering, Syiah Kuala University, Darussalam, Banda Aceh, Indonesia
H. M. Sadida ; Department of Mechanical and Industrial Engineering, Universitas Gadjah Mada, Yogyakarta, Indonesia

Sažetak

AISI 316L is one kind of implant materials due to its excellent mechanical properties and corrosion resistance. However, some of their mechanical and surface properties must be improved to a higher level of cobalt-based alloys and titanium properties. Shot peening is a surface treatment that improves properties on material surface. In this research, the effects of shot peening duration (0, 2, 4, 10, 20 and 30 min) on surface hardness, roughness, wettability, and corrosion in 0,9 % sodium chloride were investigated and discussed. According to the experimental results, it was found that shot peening increases both surface roughness and surface hardness compared to untreated sample. Furthermore, shot peening can reduce contact angle and corrosion rate after 2 minutes.

Ključne riječi

AISI 316L; shot-peening; roughness; hardness; corrosion