Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy

E. Tillová ; University of Žilina, Faculty of Mechanical Engineering, Žilina, Slovakia
M. Panušková ; University of Žilina, Faculty of Mechanical Engineering, Žilina, Slovakia

Puni tekst: engleski, pdf (1000 KB) str. 207-210 preuzimanja: 1.009* citiraj
APA 6th Edition
Tillová, E. i Panušková, M. (2008). Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy. Metalurgija, 47 (3), 207-210. Preuzeto s https://hrcak.srce.hr/22663
MLA 8th Edition
Tillová, E. i M. Panušková. "Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy." Metalurgija, vol. 47, br. 3, 2008, str. 207-210. https://hrcak.srce.hr/22663. Citirano 21.01.2020.
Chicago 17th Edition
Tillová, E. i M. Panušková. "Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy." Metalurgija 47, br. 3 (2008): 207-210. https://hrcak.srce.hr/22663
Harvard
Tillová, E., i Panušková, M. (2008). 'Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy', Metalurgija, 47(3), str. 207-210. Preuzeto s: https://hrcak.srce.hr/22663 (Datum pristupa: 21.01.2020.)
Vancouver
Tillová E, Panušková M. Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy. Metalurgija [Internet]. 2008 [pristupljeno 21.01.2020.];47(3):207-210. Dostupno na: https://hrcak.srce.hr/22663
IEEE
E. Tillová i M. Panušková, "Effect of solution treatment on intermetallic phases morphology in AlSi9Cu3 cast alloy", Metalurgija, vol.47, br. 3, str. 207-210, 2008. [Online]. Dostupno na: https://hrcak.srce.hr/22663. [Citirano: 21.01.2020.]

Sažetak
In the present work was investigated the influence of solution treatment by 505°C, 515°C and 525°C±2°C with different holding times 2, 4, 8, 16 and 32 hours on microstructural elements of commercial AlSi9Cu3 cast alloy. During this heat treatment was observed the spheroidization of eutectic Si, gradual disintegration of iron rich intermetallic phases on base Al(FeMnMg)Si, shortening and thinning of Al5FeSi iron needles and the dissolving of Al-Al2Cu-Si intermetallic phase by temperature 525°C.

Ključne riječi
Al-Si cast alloys; eutectic Si; solution treatment; intermetallic phases