Effect of hot rolling temperature on microstructures and textures of grain oriented silicon steel

C. J. Wang ; College of Applied Technology, University of Science and Technology Liaoning, Anshan, Liaoning, China
Q. Guo ; Cold Rolling Silicon Plant, Ansteel Co. Ltd., Anshan, Liaoning, China
Y. Y. Shao ; College of Applied Technology, University of Science and Technology Liaoning, Anshan, Liaoning, China


Puni tekst: engleski pdf 316 Kb

str. 216-218

preuzimanja: 359

citiraj


Sažetak

The effect of hot rolling temperature on microstructures and textures of grain oriented silicon steel was studied by optical microscopy (OM), zeiss ultra 55 Scanning electron microscope (SEM) and Electron backscatter diffraction (EBSD) technique respectively. The results show that being hot rolled at 1 152 °C and 1 227 °C respectively, the effect of hot rolling temperature on microstructures of hot rolled and normalized sheets is little, and there is only a small difference in grain size between the samples. Secondary recrystallization is difficult to occur in the medium temperature sample due to the lack of sufficient inhibitors in the sample. The major deformed texture component in center region of hot rolled sheets is {114}<481> which has obviously heredity, and it is more sharp in low temperature sample.

Ključne riječi

grain oriented silicon steel; hot rolling; sheet; texture; microstructure