Research on model of 6005A aluminum alloy

H. Q. Zhang ; College of Mechanical Engineering, North China University of Science and Technology, Hebei, Tangshan, China
H. C. Ji orcid id orcid.org/0000-0002-1592-6362 ; College of Mechanical Engineering, North China University of Science and Technology, Hebei, Tangshan, China
W. C. Pei ; College of Mechanical Engineering, North China University of Science and Technology, Hebei, Tangshan, China
Y. G. Li ; College of Mechanical Engineering, North China University of Science and Technology, Hebei, Tangshan, China


Puni tekst: engleski pdf 265 Kb

str. 261-264

preuzimanja: 360

citiraj


Sažetak

The deformation behavior of 6005A aluminum alloy at a strain rate of 0,01-10s-1, a deformation temperature of 673- 773K and a total strain of 0,8 was studied. Using the stress-strain data of 6005A aluminum alloy with a strain of 0,05-0,8, an Arrhenius-type constitutive model was established. And verified the accuracy of the model. The results show that: the flow stress of 6005A aluminum alloy increases with the increase of strain rate, and decreases with the increase of deformation temperature; Under different strains, the correlation coefficient (R) between the experimental value and the predicted value is as high as 98 %, and the average relative error (AARE) is less than 10 %, indicating that the established model has high predictability.

Ključne riječi

6005A aluminum alloy; extrusion; temperature; true stress-true strain curves; Arrhenius constitutive model