Effect graphite on magnesium diboride superconductivity synthesized by combustion method under argon pressure: Part I

S. Tolendiuly ; Satbayev University, Almaty, Kazakhstan
K. A. Alipbayev ; Almaty University of Power Engineering and Telecommunications , Almaty, Kazakhstan
S. M. Fomenko ; Satbayev University, Almaty, Kazakhstan
A. Sovet ; Almaty University of Power Engineering and Telecommunications , Almaty, Kazakhstan
A. Zhauyt ; Almaty University of Power Engineering and Telecommunications , Almaty, Kazakhstan


Puni tekst: engleski pdf 561 Kb

str. 285-288

preuzimanja: 261

citiraj


Sažetak

Solid-state synthesis of a superconductor based on magnesium diboride doped by graphite microparticles (MgB2@C) at argon atmosphere has been described. The offered method allows the possibility to increase the critical current density of the studied samples at relatively low temperature in the inert environment. The superconducting characteristics of samples critical current density (Jc) and critical transition temperature (Tc) have been measured. The impact of the doping additives on superconducting characteristics of magnesium diboride has been analyzed. The results showed that the best optimal characteristics are for MgB2@3%C that reveals a good critical transition temperature 38,8 K and the higher critical current density 2,7 x 106 A / cm2 at 5 K.

Ključne riječi

magnesium diboride; graphite microparticle; solid-state synthesis; superconductivity; temperature