Mehanička svojstva i mikrostrukturna karakterizacija Au-Pt dentalne slitine

R. Rudolf ; Faculty of Mechanical Engineering, University of Maribor, Maribor, Slovenia
T. Zupančič Hartner ; Zlatarna Celje, Celje, Slovenia
L. Kosec ; Faculty of Natural Sciences and Engineering, University of Ljubljana, Ljubljana, Slovenia
A. Todorović ; Faculty of Stomatology University of Belgrade, Belgrade, Serbia
B. Kosec ; Faculty of Natural Sciences and Engineering, University of Ljubljana, Ljubljana, Slovenia
I. Anžel ; Faculty of Mechanical Engineering, University of Maribor, Maribor, Slovenia

Sažetak

Razvoj dentalne slitine s visokim sadržajem zlata zasnovan je na ternarnom sustavu Au-Pt-Zn s nominalnim sastavom 86,9Au-9,9Pt-1,5Zn i oko 1,5 mas. % mikrolegirajučih elemenata (In, Ir, Rh). Rezultati analize su pokazali da se u slučaju slitine odžarene kod 1223 K u trajanju od 30 minuta i zakaljena u vodi optimalna mehanička svojstva i tvrdoća Au-Pt-Zn slitine mogu postići kombinacijom toplinske obrade na 720 oC u trajanju 20 minuta s naknadnim sporim hlađenjem. Rezultati istraživanja su potvrdili da se mikrostruktura Au-Pt-Zn slitine sastoji od dvije faze: _1-faze bogate sa zlatom (primarna faza) i _2 - faze bogate s platinom (sekundarna faza). Tijekom XRD analize i primjenom Rietveldove metode utvrđeno je da je sadržaj _1-faze oko 98,5 mas. %, dok je sadržaj _2-faze iznosio oko 1,5 mas. %. STA analiza je pokazala da je Au-Pt-Zn slitina imala solidus temperaturu oko 1292 K, a likvidus temperaturu oko 1412 K.

Ključne riječi

Au dentalna slitina; karakterizacija; mikrostruktura; svojstva