The influence of the base material surface preparation on the properties of thermally sprayed coatings

V. Marušić ; Faculty of Mechanical Engineering, University of Osijek, Slavonski Brod, Croatia
S. Aračić ; Faculty of Mechanical Engineering, University of Osijek, Slavonski Brod, Croatia
I. Samardžić ; Faculty of Mechanical Engineering, University of Osijek, Slavonski Brod, Croatia

Puni tekst: engleski, pdf (274 KB) str. 53-56 preuzimanja: 369* citiraj
APA 6th Edition
Marušić, V., Aračić, S. i Samardžić, I. (2010). The influence of the base material surface preparation on the properties of thermally sprayed coatings. Metalurgija, 49 (1), 53-56. Preuzeto s https://hrcak.srce.hr/40252
MLA 8th Edition
Marušić, V., et al. "The influence of the base material surface preparation on the properties of thermally sprayed coatings." Metalurgija, vol. 49, br. 1, 2010, str. 53-56. https://hrcak.srce.hr/40252. Citirano 16.12.2019.
Chicago 17th Edition
Marušić, V., S. Aračić i I. Samardžić. "The influence of the base material surface preparation on the properties of thermally sprayed coatings." Metalurgija 49, br. 1 (2010): 53-56. https://hrcak.srce.hr/40252
Harvard
Marušić, V., Aračić, S., i Samardžić, I. (2010). 'The influence of the base material surface preparation on the properties of thermally sprayed coatings', Metalurgija, 49(1), str. 53-56. Preuzeto s: https://hrcak.srce.hr/40252 (Datum pristupa: 16.12.2019.)
Vancouver
Marušić V, Aračić S, Samardžić I. The influence of the base material surface preparation on the properties of thermally sprayed coatings. Metalurgija [Internet]. 2010 [pristupljeno 16.12.2019.];49(1):53-56. Dostupno na: https://hrcak.srce.hr/40252
IEEE
V. Marušić, S. Aračić i I. Samardžić, "The influence of the base material surface preparation on the properties of thermally sprayed coatings", Metalurgija, vol.49, br. 1, str. 53-56, 2010. [Online]. Dostupno na: https://hrcak.srce.hr/40252. [Citirano: 16.12.2019.]

Sažetak
Using specimens, a research was conducted to determine the influence of the base material surface preparation for 42CrMo4 on the final coating, prior to actual thermal spraying. During thermal spraying, an Al-Ni-alloy was used as an interlayer before the actual coating with Cr-Mo-Ni. The surface hardness and the hardness distribution across the thickness of the sprayed coating were measured and the structure of respective sprayed coatings was photographed. A comparison of experimental results enabled the identification of the particular material preparation method with an optimal ratio of the satisfactory coating thickness and its hardness.

Ključne riječi
thermal spraying; gas flame; surface preparation; hardness; steel 42CrMo4