Izvorni znanstveni članak

Erosion of ductile cast iron with quartz particles

Krešimir Grilec ; University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, Ivana Lučića 5, 10000 Zagreb, Croatia
Suzana Jakovljević ; University of Zagreb, Faculty of Mechanical Engineering and Naval Architecture, Ivana Lučića 5, 10000 Zagreb, Croatia
Denis Prusac ; Technical school Zadar, Nikole Tesle 9c, 23000 Zadar, Croatia

Puni tekst: engleski, pdf (455 KB) str. 17-22 preuzimanja: 859* citiraj
APA 6th Edition
Grilec, K., Jakovljević, S. i Prusac, D. (2010). Erosion of ductile cast iron with quartz particles. Tehnički vjesnik, 17 (1), 17-22. Preuzeto s https://hrcak.srce.hr/50599
MLA 8th Edition
Grilec, Krešimir, et al. "Erosion of ductile cast iron with quartz particles." Tehnički vjesnik, vol. 17, br. 1, 2010, str. 17-22. https://hrcak.srce.hr/50599. Citirano 25.02.2021.
Chicago 17th Edition
Grilec, Krešimir, Suzana Jakovljević i Denis Prusac. "Erosion of ductile cast iron with quartz particles." Tehnički vjesnik 17, br. 1 (2010): 17-22. https://hrcak.srce.hr/50599
Harvard
Grilec, K., Jakovljević, S., i Prusac, D. (2010). 'Erosion of ductile cast iron with quartz particles', Tehnički vjesnik, 17(1), str. 17-22. Preuzeto s: https://hrcak.srce.hr/50599 (Datum pristupa: 25.02.2021.)
Vancouver
Grilec K, Jakovljević S, Prusac D. Erosion of ductile cast iron with quartz particles. Tehnički vjesnik [Internet]. 2010 [pristupljeno 25.02.2021.];17(1):17-22. Dostupno na: https://hrcak.srce.hr/50599
IEEE
K. Grilec, S. Jakovljević i D. Prusac, "Erosion of ductile cast iron with quartz particles", Tehnički vjesnik, vol.17, br. 1, str. 17-22, 2010. [Online]. Dostupno na: https://hrcak.srce.hr/50599. [Citirano: 25.02.2021.]

Sažetak
Ductile cast iron has high fatigue strength due to the spherical shape of graphite, especially after quenching and tempering. Higher toughness can be achieved by austempering. One of the advantages of ductile cast iron in relation to other cast irons is its good wear resistance. In the experiments, samples of ductile cast iron and austempered ductile cast iron were eroded with quartz sand particles at six different angles of impact (15°, 30°, 45°, 60°, 75° and 90°). The test results were presented as the loss of mass which occured during the test. Testing with quartz sand shows that the particle erosion resistance of ductile cast iron was better than that of austempered ductile iron for all impact angles except for 60°. The maximum measured wears of ductile cast iron and austempered ductile iron were at 75°.

Ključne riječi
austempered ductile cast iron; ductile cast iron; particle erosion