Izvorni znanstveni članak

Charpy notch toughness and hardness of reheated martensite and lower bainite

F. Vodopivec ; Institute of Metals and technology, Ljubljana, Slovenia
B. Šuštaršič ; Institute of Metals and technology, Ljubljana, Slovenia
J. Vojvodič-Tuma ; Institute of Metals and technology, Ljubljana, Slovenia
G. Kosec ; SIJ, Acroni d.d. Jesenice, Slovenia

Puni tekst: engleski, pdf (665 KB) str. 149-154 preuzimanja: 756* citiraj
APA 6th Edition
Vodopivec, F., Šuštaršič, B., Vojvodič-Tuma, J. i Kosec, G. (2010). Charpy notch toughness and hardness of reheated martensite and lower bainite. Metalurgija, 49 (3), 149-154. Preuzeto s https://hrcak.srce.hr/51434
MLA 8th Edition
Vodopivec, F., et al. "Charpy notch toughness and hardness of reheated martensite and lower bainite." Metalurgija, vol. 49, br. 3, 2010, str. 149-154. https://hrcak.srce.hr/51434. Citirano 16.09.2019.
Chicago 17th Edition
Vodopivec, F., B. Šuštaršič, J. Vojvodič-Tuma i G. Kosec. "Charpy notch toughness and hardness of reheated martensite and lower bainite." Metalurgija 49, br. 3 (2010): 149-154. https://hrcak.srce.hr/51434
Harvard
Vodopivec, F., et al. (2010). 'Charpy notch toughness and hardness of reheated martensite and lower bainite', Metalurgija, 49(3), str. 149-154. Preuzeto s: https://hrcak.srce.hr/51434 (Datum pristupa: 16.09.2019.)
Vancouver
Vodopivec F, Šuštaršič B, Vojvodič-Tuma J, Kosec G. Charpy notch toughness and hardness of reheated martensite and lower bainite. Metalurgija [Internet]. 2010 [pristupljeno 16.09.2019.];49(3):149-154. Dostupno na: https://hrcak.srce.hr/51434
IEEE
F. Vodopivec, B. Šuštaršič, J. Vojvodič-Tuma i G. Kosec, "Charpy notch toughness and hardness of reheated martensite and lower bainite", Metalurgija, vol.49, br. 3, str. 149-154, 2010. [Online]. Dostupno na: https://hrcak.srce.hr/51434. [Citirano: 16.09.2019.]

Sažetak
A high strength low alloyed (HSLA) V-Nb steel was heat treated to martensite and lower bainite with different grain size, reheated for 3 seconds at 750 °C and air cooled. Charpy notch tests were performed from -100 °C to 60 °C and the hardness assessed at room temperature. For as delivered steel and lower bainite, the upper shelf toughness was above 200 J and the transition temperature low, while, for martensite the upper shelf toughness threshold was aproximateky at 0 °C. After reheating, notch toughness was decreased moderatly for martensite and strongly for lower bainite. Independently on grain size, lower bainite was more propensive than martensite to embritlement after short reheating in the (α + β) range. For martensite, the change of notch toughness was not related to change of hardness, as by lower hardness lower, also toughness was lower.

Ključne riječi
HSLA steel; martensite; lower bainite; reheating; Charpy notch toughness; hardness