I. Samardžić ; Mechanical Engineering Faculty, J.J. Strossmayer University of Osijek, Slavonski Brod, Croatia
B. Mateša ; Mechanical Engineering Faculty, J.J. Strossmayer University of Osijek, Slavonski Brod, Croatia
I. Kladarić ; Mechanical Engineering Faculty, J.J. Strossmayer University of Osijek, Slavonski Brod, Croatia

Puni tekst: engleski, pdf (407 KB) str. 159-162 preuzimanja: 674* citiraj
APA 6th Edition
Samardžić, I., Mateša, B. i Kladarić, I. (2011). The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel. Metalurgija, 50 (3), 159-162. Preuzeto s https://hrcak.srce.hr/64375
MLA 8th Edition
Samardžić, I., et al. "The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel." Metalurgija, vol. 50, br. 3, 2011, str. 159-162. https://hrcak.srce.hr/64375. Citirano 24.09.2020.
Chicago 17th Edition
Samardžić, I., B. Mateša i I. Kladarić. "The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel." Metalurgija 50, br. 3 (2011): 159-162. https://hrcak.srce.hr/64375
Harvard
Samardžić, I., Mateša, B., i Kladarić, I. (2011). 'The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel', Metalurgija, 50(3), str. 159-162. Preuzeto s: https://hrcak.srce.hr/64375 (Datum pristupa: 24.09.2020.)
Vancouver
Samardžić I, Mateša B, Kladarić I. The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel. Metalurgija [Internet]. 2011 [pristupljeno 24.09.2020.];50(3):159-162. Dostupno na: https://hrcak.srce.hr/64375
IEEE
I. Samardžić, B. Mateša i I. Kladarić, "The influence of heat treatment on properties of three-metal explosion joint: AlMg-Al-Steel", Metalurgija, vol.50, br. 3, str. 159-162, 2011. [Online]. Dostupno na: https://hrcak.srce.hr/64375. [Citirano: 24.09.2020.]

Sažetak
The procedure of welding by explosion is as technical optimal solution of ship-shell parts joining frequently used in shipbuilding industry at transition three-metal joint: AlMg4.5-Al-St.52-3 working out. The investigations of mechanical and metallographic properties of joints, exposed on heat treatment at different temperatures levels, are performed. The results of mechanical and metallographic examinations of transition joints at elevated temperatures, direct on its use below 300 °C. The additional melting welding working out is in closeness of explosion- welded joint allowed.

Ključne riječi
heat treatment; three-metal explosion joint; metallographic and mechanical joints properties