J. Przondziono ; Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland
W. Walke ; Faculty of Biomedical Engineering, The Silesian University of Technology, Gliwice, Poland
E. Hadasik ; Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland
J. Szala ; Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland
J. Wieczorek ; Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland


Puni tekst: engleski pdf 824 Kb

str. 243-246

preuzimanja: 1.026

citiraj


Sažetak

The purpose of the study was to evaluate resistance to electrochemical corrosion of magnesium alloy WE43 after plastic working. Potentiodynamic and immersion corrosion tests were performed in solutions with concentration of 0,01 – 2 M NaCl. The tests of microstructure of magnesium alloy after its exposure in NaCl solutions were performed with application of scanning microscope. The results of measurements of alloy surface topography were given, which were obtained by means of optical profile measurement gauge. The results of carried out tests prove explicitly that corrosion properties of extruded magnesium alloy WE43 deteriorate with the increase of molar concentration of NaCl solution. It was proved that irrespective of the concentration of the solution, WE43 alloy features pitting corrosion. It indicates the necessity to apply protective layers on the parts made of the tested alloy.

Ključne riječi

magnesium alloy WE43 after extrusion; electrochemical corrosion; potentiodynamic and immersion tests; SEM; surface topography