Thermal analysis of high temperature phase transformations of steel

K. Gryc ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
B. Smetana ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
M. Žaludová ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
K. Michalek ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
M. Tkadlečková ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
J. Dobrovská ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
L. Socha ; VŠB-TU Ostrava, Faculty of Metalurgy and Materials Engineering, Ostrava, Czech Republic
L. Válek ; ArcelorMittal Ostrava a.s., Research, Ostrava, Czech Republic
R. Pachlopnik ; ArcelorMittal Ostrava a.s., Research, Ostrava, Czech Republic

Sažetak

The series of thermal analysis measurements of high temperature phase transformations of real grain oriented electrical steel grade under conditions of two analytical devices (Netzsch STA 449 F3 Jupiter; Setaram SETSYS 18_TM) were carried out. Two thermo analytical methods were used (DTA and Direct thermal analysis). The different weight of samples was used (200 mg, 23 g). The stability/reproducibility of results obtained by used methodologies was verified. The liquidus and solidus temperatures for close to equilibrium conditions and during cooling (20 °C/min; 80 °C/min) were determined. It has been shown that the higher cooling rate lead to lower temperatures for start and end of solidification process of studied steel grade.

Ključne riječi

steel; thermal analysis; liquidus temperature; solidus temperature