Study on interface reaction characteristics between different acidity and alkalinity slag

S. Qiu ; University of Science and Technology Liaoning, Anshan, China
J. H. Liu ; University of Science and Technology Liaoning, Anshan, China
Z. J. He ; University of Science and Technology Liaoning, Anshan, China
H. Di ; University of Science and Technology Liaoning, Anshan, China
C. Tian ; University of Science and Technology Liaoning, Anshan, China
R. R. Yin ; University of Science and Technology Liaoning, Anshan, China
J. H. Zhang ; University of Science and Technology Liaoning, Anshan, China


Puni tekst: engleski pdf 335 Kb

str. 25-28

preuzimanja: 499

citiraj


Sažetak

In this paper, the interface reaction between different acidity and alkalinity of slag was explored by comparing the changing of wetting angle and viscosity in the interface between the binary slags. And the results indicated that, the reaction temperature range of Al2O3 and basic slag was relatively larger when the reaction interface was acid slag, and the fusion temperature would change when the content of calcium and magnesium were changed in the base slag. Al2O3, SiO2 are prone to react with other components and formed the new silicate phase compared to CaO, MgO, what made interfacial diffusion relatively better.

Ključne riječi

molten slag wetting; acidity/alkalinity; viscosity; fusion temperature; scanning electron microscope (SEM)