Determination of the Change in Electrical Conductivity of Single, Bimetallic and Trimetallic Cylindrical Billets with Plastic Deformation Induced by Upsetting Process

Isik Cetintav ; Trakya University, Engineering Faculty, Edirne, Turkey
Cenk Misirli ; Trakya University, Engineering Faculty, Edirne, Turkey
Yilmaz Can ; Trakya University, Engineering Faculty, Edirne, Turkey

Sažetak

In this study, measurement of the effect of singular, bimetallic and multimetallic materials exposed to cold plastic deformation on electrical conductivity properties was investigated. The main subject of this research is plastic deformation occurring in the upsetting process and changing the conductivity properties of the parts. In the experiments, steel, aluminium, copper, brass, bimetallic and multimetallic materials designed with different combinations of these materials were used as test materials. Experimental upsetting tests were performed as a height reduction ratio 10%, 20% and 30%. The electrical conductivity measurement results of the deformed samples were obtained with a conductivity measuring device. The results obtained from the experiments are presented in graphs with electrical conductivity axis that change due to deformation. As a result of the experiments and measurements, it was concluded that the electrical conductivity of the deformed materials generally decreased slightly due to the plastic deformation of the deformed materials, and the bimetallic and multimetallic materials were similar to the properties of the majority material.

Ključne riječi

aluminium; bimetallic; brass; conductivity; copper; deformation; electrical; steel; trimetallic