Short-term low-temperature glow discharge nitriding of 316L austenitic steel

T. Frączek ; Czêstochowa University of Technology, Czêstochowa, Poland
M. Olejnik ; Czêstochowa University of Technology, Czêstochowa, Poland
J. Jasiñski ; Czêstochowa University of Technology, Czêstochowa, Poland
Z. Skuza ; Czêstochowa University of Technology, Czêstochowa, Poland


Puni tekst: engleski pdf 415 Kb

str. 151-154

preuzimanja: 610

citiraj


Sažetak

The AISI 316L austenitic steel after glow discharge nitriding at temperature of T = 673 K and duration of τ=14,4 ks, for two different variants of specimen arrangement in the glow-discharge chamber was investigated. In order to assess the effectiveness of nitriding process, the surface layers profile analysis examination, surface hardness and hardness profile examination, the analysis of surface layer structures and corrosion resistance tests were performed. It has been found that application of a booster screen effects in a nitrogen diffusion depth increment into the 316L austenitic steel surface, what results in the surface layer thickness escalation.

Ključne riječi

austenitic stainless steel; glow discharge nitriding; surface layer; hardness