Refining processes in the copper casting technology

S. Rzadkosz ; AGH - University of Science and Technology, Faculty of Foundry Engineering, Krakow, Poland
M. Kranc ; Foundry Research Institute, Krakow, Poland
A. Garbacz-Klempka ; AGH - University of Science and Technology, Faculty of Foundry Engineering, Krakow, Poland
J. Kozana ; AGH - University of Science and Technology, Faculty of Foundry Engineering, Krakow, Poland
M. Piękoś ; AGH - University of Science and Technology, Faculty of Foundry Engineering, Krakow, Poland

Abstract

The paper presents the analysis of technology of copper and alloyed copper destined for power engineering casts. The casts quality was assessed based on microstructure, chemical content analysis and strength properties tests. Characteristic deoxidising (Logas, Cup) and modifying (ODM2, Kupmod2) formulas were used for the copper where high electrical conductivity was required. Chosen examples of alloyed copper with varied Cr and Zr content were studied, and the optimal heat treatment parameters were tested for a chosen chromium copper content, based on the criterion of hardness and electrical conductivity tests. Searching for materials with high wear resistance, the influence of variable silicone content on the properties of CuNiSi alloy was researched.

Keywords

copper; casting technology; refining alloy; microstructure; properties