High-temperature characteristics of 20MnB4 and 30MnB4 micro-addition cold upsetting steels and C45 and C70 high-carbon-steels
S. Sawicki
; Czestochowa University of Technology, Czestochowa, Poland
H. Dyja
; Czestochowa University of Technology, Czestochowa, Poland
A. Kawałek
; Czestochowa University of Technology, Czestochowa, Poland
M. Knapiński
; Czestochowa University of Technology, Czestochowa, Poland
M. Kwapisz
; Czestochowa University of Technology, Czestochowa, Poland
K. Laber
; Czestochowa University of Technology, Czestochowa, Poland
Sažetak
The paper analyzes the high-temperature plasticity characteristics of 20MnB4 and 30MnB4 with micro-additives, intended for cold upsetting and high-carbon steels C45 and C70 in the “solid phase-liquid” during heating and cooling. The investigation was conducted to determine the plastic formability of the examined alloy under hot plastic working conditions. Experiments were carried out on the simulator Gleeble 3800 with the aim of determining the susceptibility of 20MnB4, 30MnB4, C45 and C70 steels to cracking at high temperature. The nil strength (NST), nil ductility (NDT) and ductility recovery temperatures (DRT), and the fracture toughness factor and the BRT (brittleness temperature range) have been determined.
Ključne riječi
plasticity; alloy steel; high – carbon steel; temperature; mechanical properties